1) High-Temperature Reduction Process
高温还原工艺
2) reduction process
还原工艺
1.
A mathematical model of the relation between molybdenum powder particle, oxygen content and reduction process parameters has been established by means of quadratic general rotary unitize design.
采用二次通用旋转组合设计法,建立了钼粉粒度、氧含量与还原工艺参数间关系的经验数学模型,绘制了双工艺参数与钼粉粒度、氧含量间关系的函数图,得出了制备钼粉的最佳工艺,即还原温度为950~1000℃,料层厚度为1。
3) high temperature reduction
高温还原
1.
The main factors of affecting the reduction of Cr2O3 in synthetic chromite briquette by carbon at high temperature, and the condensation, growth and separating behavior of metal phase from slag phase during reduction at high temperature reduction have been researched.
研究了含碳铬矿团块在高温还原过程中影响Cr2O3还原的主要因素,以及含碳铬矿团块在高温还原过程中金属相的聚集长大及其与渣相的分离状态。
4) reductive ECB process
还原ECB工艺
5) self-reduction under high temperature
高温自还原
6) high temperature technology
高温工艺
1.
The effects of live yeast cell derivative (LYCD) by Moutai high temperature technology were discussed in this paper.
结果表明,传统的茅台酒高温工艺能有效刺激酿酒酵母MT281LYCD产生的生物活性;应激发生在50℃和45min时,制备的LYCD活性最强。
补充资料：高温氧化还原法
分子式：
CAS号：
性质：是国际原子公司研究的后处理方法，主要包括两个化学反应：氧化3UO2+O2U3O8还原 U3O8+2H23UO2+2H2O在沿元件长度每隔1～2.5cm打一个孔，在高温下氧化。氧化物体积膨胀，包壳破裂。氧化得八氧化三铀再还原成二氧化铀，如此反复三次。得到的二氧化铀氟化后再浓缩235U的含量，制成小片，烧结成片状燃料。铀在氧化、还原处理过程中得到了部分净化，部分裂变产物被去除。氙、氪、碘和铯被去除，90％钌,一半的锝、镉、铟和少量的钼和铌被去除。
CAS号：
性质：是国际原子公司研究的后处理方法，主要包括两个化学反应：氧化3UO2+O2U3O8还原 U3O8+2H23UO2+2H2O在沿元件长度每隔1～2.5cm打一个孔，在高温下氧化。氧化物体积膨胀，包壳破裂。氧化得八氧化三铀再还原成二氧化铀，如此反复三次。得到的二氧化铀氟化后再浓缩235U的含量，制成小片，烧结成片状燃料。铀在氧化、还原处理过程中得到了部分净化，部分裂变产物被去除。氙、氪、碘和铯被去除，90％钌,一半的锝、镉、铟和少量的钼和铌被去除。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条