1) intergranular amorphous phase
晶间非晶相
1.
In the present study, an intergranular amorphous phase was successfully induced in the Nd_2Fe_(14)B/α-Fe nanocomposite magnets by controlling the process of the melt solidification by changing the wheel speed.
本文通过改变快淬速度来控制 NdFeCoB 合金熔体的凝固过程,成功地在 Nd_2Fe_(14)B/α-Fe 复合纳米晶引入了晶间非晶相。
2) crystal-amorphous interphase
结晶-非晶中间相
3) Amorphous phase
非晶相
1.
The results show that niobium addition promotes the formation of amorphous phase and stabilizes the amorphous phase.
结果表明:添加Nb可以在甩带过程中促进非晶的形成并稳定非晶相;在退火过程中,加入Nb后形成的析出相可以抑制晶粒长大,使晶粒细化且分布均匀,进而大幅度提高了材料的综合磁性能。
2.
At different annealing temperatures,the magnetic properties,saturation magnetostriction and Curie temperature of amorphous phase of the Co_(66)Fe_4Mo_2Si_(16)B_(12) alloy were investigated by a ballistic galvanometer,small-angle magnetization tester and core tester.
结果表明:Co66Fe4Mo2Si16B12合金经退火后非晶相和剩余非晶相的居里温度随退火温度升高而提高;Co66Fe4Mo2Si16B12合金经高于500℃退火后磁性能变坏,是饱和磁致伸缩系数变大所致。
3.
The results show that the powders of both Ti and Al have a trend of refining along with ball milling time,an amorphous phase occurs after 5 h milling and then a full amorphous phase develops after 20 h milling.
结果表明,Ti和A l的粉末随着球磨时间的延长有明显地细化趋势,球磨5h后产生非晶,20 h后完全接近非晶相。
4) Amorphous SiO2
SiO2非晶相
1.
Amorphous SiO2 formed .
透射电镜亚微米纳米尺度分析表明,该石英脉中存在一种已部分转变成α-石英纳米晶的SiO2非晶相,且观察到类似于柯石英假象的胀裂现象。
5) Homogeneous Amorphous
均相非晶
6) amorphous phase
非晶形相
补充资料：肥皂介晶相
分子式：
CAS号：
性质：肥皂相行为名称之一。固态肥皂随温度升高能渐变成液状，从起始熔点到最终熔点之间存在着许多相的过渡，每个相均具有明显的相界限和相变点，这种状态称之谓肥皂介晶相。介晶相的温度范围从40～50℃到250℃之间。
CAS号：
性质：肥皂相行为名称之一。固态肥皂随温度升高能渐变成液状，从起始熔点到最终熔点之间存在着许多相的过渡，每个相均具有明显的相界限和相变点，这种状态称之谓肥皂介晶相。介晶相的温度范围从40～50℃到250℃之间。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条