1) Sandwich Molding
三明治成形
2) multi-point sandwich forming
多点"三明治"成形
1.
Experimental research on the saddle workpiece by multi-point sandwich forming;
马鞍形板材件多点“三明治”成形实验研究
3) cut the sandwich in two.
把三明治切成两半
4) sandwich
[英]['sænwɪtʃ] [美]['sænwɪtʃ]
三明治
1.
Function and morphological characteristics of Chinese experimental suckling mini-pig hepatocytes cultured in sandwich;
三明治培养新生实验小型猪肝细胞的功能与形态
2.
Patato sandwich was made by patato as the main material and carrot and pork as supplementary material.
本实验以马铃薯为主要原料,通过添加胡萝卜、猪肉等辅料研制马铃薯三明治,并对其配方和工艺进行了初步探索和研究。
3.
Iron/aluminium foam/iron and titanium/aluminium foam/titanium sandwiches were prepared by powder metallurgical foaming method.
采用粉末冶金发泡法制备了Fe Al Fe、Ti Al Ti泡沫铝芯三明治结构 ,研究了泡沫铝芯的膨胀规律 ,分析了面板与泡沫铝芯的冶金结合过程 ,提出了微观结合机制。
5) sandwich beams
三明治梁
1.
Deformation of sandwich beams with spherical pore Al alloy foam core in three-point bending;
球形孔泡沫铝合金三明治梁的三点弯曲变形
2.
The failure modes and peak loads of sandwich beams with this Al alloy foam core were measured which was in good agreement with theoretic values.
研究了高比强泡沫铝合金和泡沫纯铝的单向压缩和剪切性能,对以高比强泡沫铝合金为夹芯的三明治梁失效模式的尺寸范围和承载能力进行了理论计算,结果与实验结果符合得很好。
6) Sandwich treatment
三明治法
1.
Sandwich treatment of interventional chemotherapy ,3D-CRT and interventional chemotherapy was given .
目的探讨三明治法对晚期肺癌的近期疗效。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。