1) In-situ reaction sintering
原位反应液相烧结
2) liquid reactive sintering
液相反应烧结
1.
The composites of different Mo/Si ratio were prepared by vacuum liquid reactive sintering.
利用液相反应烧结制备不同配比的Mo-S i复合材料,用X射线分析相组成,扫描电镜观察微观组织形貌,热膨胀仪测不同块体材料的热膨胀系数(CTE)。
3) reactive liquid phase sintering
反应液相烧结
1.
The result shows that these dense materials can be got by the reactive liquid phase sintering, with powders of B-Fe as raw material and Fe as reactive dose and adhesive agent.
结果表明，以 Ｂ-Ｆｅ粉为原料，以 Ｆｅ粉作为反应剂和粘结剂来制备这种脆性材料，利用其反应液相烧结可以达到较致密的程度。
2.
The reaction equation of sintering CeB6 and reactive liquid phase sintering mechanism were studied.
以氢直流电弧法制备CeHx纳米粉末,再采用放电等离子(SPS)反应液相烧结纳米CeHx和微米B的混合粉末,制备了高性能CeB6多晶块体热阴极材料。
4) in situ reaction sintering
原位反应烧结
1.
porous SiC woodceramics with quasi-log microstructure were prepared from wood powder,epoxide resin and silicon powder through the following steps: carbonizing at preset temperature for 2h,and in situ reaction sintering at 1000-1600℃ for 1h.
以香杉木粉、硅粉和环氧树脂为原料,先低温制成木材陶瓷,然后利用高温原位反应烧结工艺制成了具有原木微观结构的SiC多孔木材陶瓷。
2.
The needle-like structured porous mullite ceramic membrane supports were prepared us- ing kaolin,Al_2O_3 and Al(OH)_3 as raw materials by in situ reaction sintering.
采用粘土矿物高岭土、Al_2O_3和Al(OH)_3为原料,原位反应烧结合成了针状结构多孔莫来石陶瓷膜载体。
6) solid phase reaction of sintering process
烧结固相反应
补充资料：粉末液相烧结
粉末液相烧结
liquid phase sintering of powder
fenmo yex一ong shaojle粉末液相烧结(liquid phase sintering ofpowder)具有两种或多种组分的金属粉末或粉末压坯在液相和固相同时存在状态下进行的粉末烧结。此时烧结温度高于烧结体中低熔成分或低熔共晶的熔点。由于物质通过液相迁移比固相扩散要快得多，烧结体的致密化速度和最终密度均大大提高。液相烧结工艺已广泛用来制造各种烧结合金零件、电接触材料、硬质合金和金属陶瓷等。 类型根据烧结过程中固相在液相中的溶解度不同，液相烧结可分为3种类型。(l)固相不溶于液相或溶解度很小，称为互不溶系液相烧结。如W一cu、w一Ag等假合金以及A12O3一Cr、A12O3一Cr一Co一Ni、A12O3一Cr-W、BeO一Ni等氧化物一金属陶瓷材料的烧结。(2)固相在液相中有一定的溶解度，在烧结保温期间，液相始终存在，称为稳定液相烧结。如Cu一Pb、w一eu一Nl、we-C。、TIN一Ni等材料的烧结。(3)因液相量有限，又因固相大量溶入而形成固溶体或化合物，使得在烧结保温后期液相消失，这类液相烧结称为瞬时液相烧结。如Fe一eu(
说明：补充资料仅用于学习参考，请勿用于其它任何用途。