1) TPU
热塑性聚氨酯弹性体(TPU)
2) TPU
热塑性聚氨酯弹性体
1.
Preparation of thermoplastic polyurethane elastomer(TPU) for ink;
油墨用热塑性聚氨酯弹性体的研制
2.
Two methods of different dynamic vulcanization processing of TPU/EVM blends in HAAKE Rheocord90 were compared in which DCP was chosen as the curing agent.
比较了通过HAAKE Rheocord90转矩流变仪用两种不同的动态硫化混炼方法对热塑性聚氨酯弹性体/乙烯-醋酸乙烯酯共聚物(TPU/EVM)共混体系性能的影响,硫化剂选用过氧化二异丙苯(DCP);探讨了密炼室转子转速和混炼温度对动态硫化共混物性能的影响。
3.
Polypropylene/TPU/nano-silica composites were prepared by melt-blending process,mechanic,crystallization and rheology properties of composites were studied.
采用熔融共混法制备了聚丙烯(PP)/热塑性聚氨酯弹性体(TPU)/纳米SiO2复合材料,研究了复合材料的力学性能、结晶性能、流变性能。
3) Thermoplastic Polyurethane
热塑性聚氨酯弹性体
1.
The blends with different ratios of high density polyethylene/thermoplastic polyurethane(HDPE/PUR-T) were prepared through melt mixing by using a twin-screw extruder,with E/VAC-g-MAH as the compatibilizer.
以高密度聚乙烯(HDPE)和热塑性聚氨酯弹性体(PUR-T)为主要原料,以马来酸酐接枝(乙烯/乙酸乙烯酯)共聚物(E/VAC-g-MAH)为增容剂,采用双螺杆挤出熔融共混技术制备了HDPE/PUR-T和HDPE/PUR-T/(E/VAC-g-MAH)等共混材料,利用60Co-γ射线源在较低辐照剂量(小于等于25 kGy)下对共混材料进行了γ-辐照。
2.
polypropylene/ thermoplastic polyurethane (PP /PUR-T) blends were prepared with co-rotating twin screws extruder.
利用双螺杆挤出机制备了聚丙烯(PP)/热塑性聚氨酯弹性体(PUR-T)共混材料,研究了这类共混材料经1~25kGy剂量的γ射线辐照前后的力学性能、动态力学行为与形态。
3.
The properties and morphology of segmented polyether thermoplastic polyurethane elastomers consisting of EO/THF copolyether and polyethelene glycol(PEG) as the soft segments and isophorone diisocyanate extended with 1,4 butanediol as the hard segments were studied by means of tensile testing, TEM, WAXD and DSC.
采用熔融预聚二步法合成了以环氧乙烷 -四氢呋喃无规共聚醚和聚乙二醇混合聚醚为软段 ,异佛尔酮二异氰酸酯和 1,4 -丁二醇为硬段的热塑性聚氨酯弹性体 ,利用 TEM、WAXD、DSC对聚合物进行了表征 ,并测试了其力学性能。
5) thermoplastic polyurethane elastomer
热塑性聚氨酯弹性体
1.
Influence of CL-20 coated with thermoplastic polyurethane elastomers (TPU) on mechanical properties of NEPE propellant;
热塑性聚氨酯弹性体包覆CL-20及对NEPE推进剂性能影响
2.
Polyoxymethylene(POM) and thermoplastic polyurethane elastomer(TPU) were blended in twin-screw extruder.
聚甲醛(POM)和热塑性聚氨酯弹性体(TPU)于不同温度下在双螺杆挤出机中共混,用扫描电镜(SEM)考察了共混试样的相形态,并对试样分散相粒径进行了统计,研究了分散相粒径随加工温度的变化。
3.
With polyamide 1010(PA1010) as matrix material and with ester-based thermoplastic polyurethane elastomer (TPU) as toughener,PA1010/TPU blends were prepared using a Haake PTW16/25p twin-screw extruder.
以尼龙1010(PA1010)为基体,以聚酯型热塑性聚氨酯弹性体(TPU)为增韧剂,采用HaakePTW16/25p型双螺杆挤出机制备了PA1010/TPU共混增韧尼龙材料,测试了PA1010/TPU共混物的表观粘度、非牛顿指数等流变参数,并重点讨论了其流变性能。
6) Thermoplastic polyurethane elastomer
聚氨酯热塑性弹性体
补充资料：聚氨酯热塑性弹性体
聚氨酯热塑性弹性体又称热塑性聚氨酯橡胶，简称TPU，是一种(AB)n型嵌段线性聚合物，A为高分子量(1000-6000)的聚酯或聚醚，B为含2-12直链碳原子的二醇，AB链段间化学结构是用二异氰酸酯，通常是MDI连接。一般的结构式为见图。热塑性聚氨酯橡胶靠分子间氢键交联或大分子链间轻度交联，随着温度的升高或降低，这两种交联结构具有可逆性。在熔融状态或溶液状态分子间力减弱，而冷却或溶剂挥发之后又有强的分子间力连接在一起，恢复原有固体的性能。
聚氨酯热塑性弹性体有聚酯型和聚醚型两类，白色无规则球状或柱状颗粒，相对密度1．10-1．25，聚醚型相对密度比聚酯型小。聚醚型玻璃化温度为100．6-106．1℃，聚酯型玻璃化温度108．9-122．8℃。聚醚型和聚酯型的脆性温度低于-62℃，硬醚型耐低温性忧于聚酯型。
聚氨酯热塑性弹性体突出的特点是耐磨性优异、耐臭氧性极好、硬度大、强度高、弹性好、耐低温，有良好的耐油、耐化学药品和耐环境性能，在潮湿环境中聚醚型酯水解稳定性远超过聚酯型。
聚氨酯热塑性弹性体无毒、无味，可溶于甲乙配、环己酮、四氢呋喃、二氧六环、二甲基甲酰胺等溶剂，也能溶于甲苯、醋酸乙酯、丁酮、丙酮以适当比例组成的混合溶剂中，呈现无色透明状态，有较好的贮存稳定性。