1) carbothermic reduction-chlorination
碳热还原氯化法
2) carbothermal reduction-nitriding
碳热还原-氯化
3) carbothermal reduction and nitridation
碳热还原氮化法
1.
One way is the hot-pressing process using chemical starting materials, and another is Carbothermal Reduction and Nitridation process using natural starting materials.
目前,制取Sialon耐火材料的途径通常有两种:(一)利用化学原料氮化法合成;(二)利用天然原料碳热还原氮化法合成。
4) carbothermal reduction nitridation
碳热还原氮化法
1.
The(Ca,Mg) α′-Sialon/BN composite powder was synthesized by carbothermal reduction nitridation with boron-rich slag as main starting material,of which the composition is(Ca,Mg)xSi12-3xAl3xOxN16-x where x is ranging from 0.
以富硼渣为主要原料,采用碳热还原氮化法合成了组分为(Ca,Mg)xSi12-3xAl3xOxN16-x(x=0。
5) carbothermal reduction
碳热还原法
1.
Effects of calcining methods and addictives on AlN powder prepared by carbothermal reduction;
煅烧方式和添加剂对碳热还原法制备氮化铝粉末的影响
2.
Preparation of LiFePO_4/C composite cathode materials by a carbothermal reduction method;
用碳热还原法制备LiFePO_4/C复合正极材料
3.
Aluminium nitride powder was prepared by carbothermal reduction process.
本文以Al2O3和活性碳为原料,采用碳热还原法制备了氮化铝陶瓷粉末。
6) Carbon thermal reduction method
碳热还原法
1.
Li3V2(PO4)3 cathode material for Li-ion battery was prepared by the carbon thermal reduction method.
采用碳热还原法制备了Li3V2(PO4)3锂离子电池正极材料,通过XRD、循环伏安和充放电测试对样品的性能进行了研究。
2.
08) was prepared by carbon thermal reduction method.
采用液相碳热还原法合成了Co改性的锂离子电池正极材料LiFe1-xCoxPO4(X=0,0。
补充资料：碳热还原法
在高温下用碳还原金属氧化物制取金属的方法。例如，在高温下用碳还原氧化亚铁可得金属铁：
FeO+C─→Fe+CO其热力学依据是：金属氧化物的生成自由能变化ΔG(MO)是随温度的升高而逐渐增高（负值变小），而一氧化碳的生成自由能变化ΔG(CO)却是随温度的升高而明显降低（负值变大）,所以当温度升高到ΔG(CO)-ΔG(MO)＜0时，原来在低温下不能进行的反应变得能够进行。这种方法的优点是焦炭价廉易得，缺点是必须使用鼓风炉或电熔炉，而且许多金属会生成碳化物。
FeO+C─→Fe+CO其热力学依据是：金属氧化物的生成自由能变化ΔG(MO)是随温度的升高而逐渐增高（负值变小），而一氧化碳的生成自由能变化ΔG(CO)却是随温度的升高而明显降低（负值变大）,所以当温度升高到ΔG(CO)-ΔG(MO)＜0时，原来在低温下不能进行的反应变得能够进行。这种方法的优点是焦炭价廉易得，缺点是必须使用鼓风炉或电熔炉，而且许多金属会生成碳化物。