2) in-situ colloidal forming process
原位凝固胶态成型工艺
1.
The less viscous dense alumina suspensions were obtained for the effective application in the in-situ colloidal forming process.
制备了低粘度、高固相含量氧化铝悬浮浆料,并将其有效地应用于原位凝固胶态成型工艺中。
3) consolidation in-situ forming
原位凝固成型
1.
A new consolidation in-situ forming process for high-performance aluminium oxide ceramic using starch as the consolidator/binder was investigated.
为获得以淀粉作凝固剂原位凝固成型氧化铝高性能陶瓷的方法,文中探讨了酯化淀粉添加量对陶瓷浆料流变特性以及成型出的素坯的线收缩、密度、干坯强度和显微结构的影响。
4) in situ gel_casting
原位凝胶浇注成型
5) in situ crosslinked hydrogel
原位固化凝胶
6) direct gel coagulation casting
直接凝胶凝固成型
1.
The thesis researched basic theory and process of a new ceramic formation method of original position congeal,which is direct gel coagulation casting(DGCC),and found basic affecting factors about the process of DGCC.
本文研究了一种新的陶瓷原位凝固成型技术 (直接凝胶凝固成型 )的基本原理和工艺过程 ,找出了影响成型工艺的基本因素 ,并且利用该成型技术制备出强度和密度较高 ,且密度均匀性好的坯体。
补充资料：金属基复合材料原位生长成型
金属基复合材料原位生长成型
in- situ fabrication of metal matrix composites
金属基复合材料原位生长成型动一sl’tu fabrica·tion of metal matrix eomposites金属在一定组成和环境条件下，局部形成增强体与原金属构成的复合材料。例如，定向凝固使参与共晶反应的a和刀两相同时从液相中以棒状或层状规则排列生长。另外，如有包晶或偏晶反应的两相合金，或成分偏离共晶成分，也能通过定向凝固使两相规则排列生长，但工艺条件苛刻。 原位生长成型必须满足3个条件:①有温度梯度的加热方式;②满足平面凝固条件;③两相的成核和生长要协调进行。二元系共晶材料的平面凝固条件为立、月丛丝鱿‘旦立V一Z人式中认为液相温度梯度，V为凝固速度，mL为液相线斜率，Q为共晶成分，Co为合金成分，及为原溶质在液相中的扩散系数。 在定向凝固设备上要求有很大的认。目前原位生长成型有功率降低法(民约30℃/cm)、快速凝固法(位约100℃/cm)、液态金属冷却法(仅约300℃/cm)、流态床急冷法(GL约300℃/cm)和区域熔化液态金属冷却法(q约1200℃/cm)。后者制备大直径试棒尚有困难，一般采用快速凝固法，因为它设备简单，操作方便，不受液态金属的污染。(胡壮麒)