1) original position solidification
原位凝固
1.
The results showed that the pore diameter distribution of the green body made by original position solidification method was more uniform and the shape was more regular than that made by dry pressing and dip casting.
研究发现:用原位凝固工艺获得的素坯比用干压和注浆成型的素坯孔径分布更加均匀、具有单峰性,孔洞形状规则。
2.
The result showed that the pore diameter distribution of the original position solidification green body was more well than dry pressing and dip casting and the distribution peak was only one, moreover, the shape of pore was more regular.
研究发现 ,用原位凝固工艺获得的素坯比用干压和注浆成型的素坯孔径分布更加均匀 ,具有单峰性 ,孔洞形状规则。
2) consolidation in-situ forming
原位凝固成型
1.
A new consolidation in-situ forming process for high-performance aluminium oxide ceramic using starch as the consolidator/binder was investigated.
为获得以淀粉作凝固剂原位凝固成型氧化铝高性能陶瓷的方法,文中探讨了酯化淀粉添加量对陶瓷浆料流变特性以及成型出的素坯的线收缩、密度、干坯强度和显微结构的影响。
3) In Situ Gelling
原位凝固技术
4) in situ crosslinked hydrogel
原位固化凝胶
5) in-situ colloidal forming process
原位凝固胶态成型工艺
1.
The less viscous dense alumina suspensions were obtained for the effective application in the in-situ colloidal forming process.
制备了低粘度、高固相含量氧化铝悬浮浆料,并将其有效地应用于原位凝固胶态成型工艺中。
补充资料：电化学原位红外光谱法
分子式：
CAS号：
性质：红外光谱法检测灵敏度高，具有“指纹”性的谱段，对于确认电化学反应过程的中间体以及了解吸附物种的状态特别有利。但是由于信号微弱，信噪比低，特别是电化学中常用的水溶液对红外线吸收强烈，使用困难较多。直至20世纪80年代，陆续采用了一些新技术，如光学电解池的聚乙烯红外窗及1～100μm薄层电解液，红外光谱的傅里叶变换技术、偏振调制技术和扫描干涉仪等，发展了如SNIFTIRS，EMIRS，IRRAS等方法，在电化学动力学、电催化、化学电源等许多方面已获得有意义的成果。
CAS号：
性质：红外光谱法检测灵敏度高，具有“指纹”性的谱段，对于确认电化学反应过程的中间体以及了解吸附物种的状态特别有利。但是由于信号微弱，信噪比低，特别是电化学中常用的水溶液对红外线吸收强烈，使用困难较多。直至20世纪80年代，陆续采用了一些新技术，如光学电解池的聚乙烯红外窗及1～100μm薄层电解液，红外光谱的傅里叶变换技术、偏振调制技术和扫描干涉仪等，发展了如SNIFTIRS，EMIRS，IRRAS等方法，在电化学动力学、电催化、化学电源等许多方面已获得有意义的成果。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条