1) remnant polarization (P_r)
剩余极化P_r
2) remnant polarization
剩余极化
1.
The highest remnant polarization 2Pr .
用溶胶-凝胶法制备了钛酸锶铋层状钙钛矿结构(SBTi)铁电陶瓷,研究了不同烧结温度对其显微结构和电性能的影响,分析了相关机理,发现1100℃烧结样品的晶粒发育比较完全,居里温度为520℃;压电常数d33和剩余极化强度2Pr较大,分别为9×10-12C/N和2。
2.
Under the electric filed of 125 kV/cm the remnant polarization (2P_(r)) of .
在测量电场强度为125kV/cm时,样品A和样品B的剩余极化(2Pr)分别为5。
3.
Vanadium-doping with appropriate content enlarges the remnant polarization (2P_ r ) and enhances the electric breakdown voltage of SrBi_ 4 Ti_ 4 O_ 15 (SBTi).
适量的钒掺杂,大大增加了SrBi4Ti4O15(SBTi)铁电材料的剩余极化2Pr,并改善了材料的耐压性能。
3) remanent polarization
剩余极化
1.
From the measurement of D-E hysteresis loops using RT6000HVS system,the remanent polarization and coercive field of SrBi 4Ti 4O 15 ceramic were found to be larger than 7μC/cm 2 and 73kV/cm respectively,and the sat.
对于SrBi4Ti4O1 5陶瓷施加 12 0kV cm的电场仍无法得到饱和的回线 ,此时的剩余极化和矫顽场分别约为 7μC cm2 和 73kV cm 。
2.
80)Ti_3O_(12)) films exhibited well-saturated polarization-electric field(P-E) switching curves with the remanent polarization(P_r) of 27 μC/cm~2 an.
80T i3O12薄膜具有较好电滞回线(P-E),在应用电压为10 V,测试频率为1MH z下,其剩余极化(Pr)及矫顽场(Ec)分别达到27μC/cm2和70 kV/cm。
3.
80 has the largest remanent polarization.
80时,薄膜具有最大的剩余极化(Pr),在应用电压为10V时,Pr及Ec分别达到27×10–6C/cm2和70×103V/cm。
4) remanent polarization
剩余极化强度
1.
Normally,the varying of the remanent polarization of the ferroelectric ceramics when temperature changes can be reflected on the pyroelectric current measurement of the ferroelectric ceramics.
通常情况利用铁电体陶瓷的热释电效应,通过测量其加热过程中产生的热释电流,可以较为准确地反映出铁电体陶瓷剩余极化强度Pr随温度的变化。
2.
The results show that the remanent polarization (Pr) is significantly enhanced,the coercive field strength (Ec) is decreased to a certain extent, and the average grain size is decreased to 1～2 μm for BTN ceramics with appropriate amounts of Nb-doping.
结果表明,适量的Nb掺杂可显著提高材料的剩余极化强度Pr,一定程度上降低矫顽场强Ec,并减小BTN陶瓷的平均晶粒尺寸(1～2μm)。
5) remnant polarization
剩余极化强度
1.
The remnant polarization of LaAlO3-BaTiO3 superlattices with LaAlO3 cap layer is 40 times larger than that of the superlattices with no cap l.
电学性能测试证明LaAlO3顶层结构的存在极大地改善了超晶格薄膜的电学性能,使其剩余极化强度增加了40多倍。
2.
The remnant polarization value decreased from 32 699 μC/cm 2 to 26 316 μC/cm 2, the coercive field was basically constant at 38 396 kV/cm, .
发现在激光未烧熔薄膜的能量密度下 ,经过激光作用后 ,PZT薄膜的铁电性能发生变化 :在外加电压为 6V时 ,剩余极化强度值Pr 从 32 6 99μC/cm2 变到 2 6 316 μC/cm2 ;矫顽电场保持为 38 396kV/cm不变 ;疲劳性能变稳定 ,在循环 1 75× 10 9次时 Pr 衰变率由 4 4 3%变为 34 7%。
3.
18%,the highest remnant polarization P,and coercive field Ec were 8.
发现在1150℃进行烧结,样品晶粒发育较完全,晶粒α轴取向较大,铁电性能优良,剩余极化强度Pr=8。
6) the surplus sees polarizability
剩余视极化率
补充资料：剩余极化强度
分子式：
CAS号：
性质：铁电体经极化处理后，当撤除外电场后，其极化强度并不为零而是保持一有限值，称为剩余极化强度，常用Pr表示。表明已经定向排列的电畴在没有足够的反向电场输入附加能量，就无法回到其原来所处的随机状态。压电陶瓷因具有剩余极化才成为具有实用价值的压电元器件。
CAS号：
性质：铁电体经极化处理后，当撤除外电场后，其极化强度并不为零而是保持一有限值，称为剩余极化强度，常用Pr表示。表明已经定向排列的电畴在没有足够的反向电场输入附加能量，就无法回到其原来所处的随机状态。压电陶瓷因具有剩余极化才成为具有实用价值的压电元器件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条