1) W/O/W multiple emulsion
W/O/W多重乳液
1.
A W/O/W multiple emulsion(ME) type crosslinker for indepth profile modification of delayed gelation was prepared from chromium acetate aqueous solution as inner dispersed phase and diesel as outer dispersed phase by using W/O emulsifier T161 and O/W emulsifier T20.
以醋酸铬水溶液为水内相,柴油为油相,T161为W/O乳化剂,T20为O/W乳化剂制备了具延缓交联作用、可用于深部调剖体系的W/O/W多重乳液交联剂。
2) W/O/W multiple emulsions
W/O/W多重乳状液
1.
Study on W/O/W multiple emulsions;
W/O/W多重乳状液的实验研究
3) Multiple Emulsion W/O/W
多重乳状液W/O/W
4) W/O emulsion
W/O乳液
1.
we research on that how to form a stable W/O emulsion with various emulsors.
石膏模具是陶瓷工业生产中长期以来使用的传统模具,为了克服石膏模具的一些缺点,研究了不饱和树脂基模具的制备,以不饱和聚酯树脂为基体,加入各种助剂配制W/O乳液,然后加入复合乳化剂,最终制得微孔模具材料。
5) water-oil-water liquid emulsion membrane
W/O/W乳状液膜
6) O/W microemulsion
O/W微乳液
1.
At first, Pd(NO3)2 was recycled from the waste Pd-C catalyst, then, the palladium nanoparticles with size of 5 nm to 200 nm were generated in the O/W microemulsion of sodium dodecyl sulfate (SDS), Brij30 and H2O system by using nonionic surfactant Brij30 as the reducing agent.
从Pd-C催化剂废料回收Pd(NO3)2,然后在SDS/Brij30/H2O体系O/W微乳液中制备纳米钯。
2.
Fine particles of polyaniline were prepared in (An+O/W microemulsion)two phase system in which the An phase was used as a monomer source and the O/W microemulsion phase for polymerization.
选择合适的SDBS／苯胺／H2O三组分O／W微乳液与苯胺单体共存的两相体系，以单体相为单体源，在O／W三组分微乳液中进行了苯胺聚合，所得聚苯胺粒子大小仅为3nm，分布较均匀，且具有较好的导电性能。
补充资料：多阶段乳液聚合
分子式：
CAS号：
性质：又称种子(乳液)聚合，两阶段(或多阶段)乳液聚合，核-壳乳液聚合或复合乳液聚合。为了得到颗粒较大的聚合物，在乳液聚合中，可先加入乳液作为种子，这样在聚合过程中，单体可在加入的种子上继续聚合，而不形成新的微粒，因此可以得到颗粒较大的聚合物，这种聚合称为种子聚合。首先，通过常规的(一般为间歇式)乳液聚合或乳液共聚合制备种子胶乳，然后在种子胶乳存在下进行另一种单体或单体混合物的聚合。是新近发展起来的一种乳液聚合方法。主要用来合成各种具有不同组分以及不同形态特征的复合聚合物胶乳。
CAS号：
性质：又称种子(乳液)聚合，两阶段(或多阶段)乳液聚合，核-壳乳液聚合或复合乳液聚合。为了得到颗粒较大的聚合物，在乳液聚合中，可先加入乳液作为种子，这样在聚合过程中，单体可在加入的种子上继续聚合，而不形成新的微粒，因此可以得到颗粒较大的聚合物，这种聚合称为种子聚合。首先，通过常规的(一般为间歇式)乳液聚合或乳液共聚合制备种子胶乳，然后在种子胶乳存在下进行另一种单体或单体混合物的聚合。是新近发展起来的一种乳液聚合方法。主要用来合成各种具有不同组分以及不同形态特征的复合聚合物胶乳。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条