1) C5 hydrogenation petroleum resin
C5加氢石油树脂
1.
Based on the behavior of self-polymerization of active components during the production of C5 hydrogenation petroleum resin,a compound inhibitor(inhibitor and dispersant) was added in the pretreatment process of raw materials.
针对C5加氢石油树脂生产过程中存在的活性组分自聚现象,在原料预处理工序中加入复合型阻聚剂(阻聚剂和分散剂)。
2) hydrogenated C5 petroleum resin
加氢C5石油树脂
1.
The compatibility of styrene-butadiene-styrene block copolymer(SBS)with hydrogenated C5 petroleum resin(HC5R)was studied by dynamic mechanical analysis.
通过动态力学分析研究了苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)与加氢C5石油树脂(HC5R)共混体系的相容性,并考察了臭氧处理对共混体系的影响。
3) C5 Petroleum Resin
C5石油树脂
1.
C5 petroleum resin applied in road marking;
C5石油树脂在路标漆中的应用
2.
Hydrogenated C5 petroleum resin was prepared with C5 petroleum resins as feedstock at 240～270℃,14～17MPa,liquid space velocity 0.
以C5石油树脂为原料,在温度为240~270℃,压力为14~17 MPa,液体空速为0。
3.
The polymerization processes of C5 petroleum resin were reviewed,the applications of C5 petroleum resin in many fields such as adhesive,coating,paint,printing ink and color asphalt wered studied,and some advice was given to the petroleum resin factories.
介绍了C5石油树脂聚合工艺,研究了C5石油树脂在胶粘剂、涂料、油漆、油墨及彩色沥青等领域的应用,并对国内石油树脂生产企业提出一些建议。
4) C_5 petroleum resin
C5石油树脂
1.
Used C_5 petroleum resin as the materials, through graft reaction, the polar groups was added onto the molecular of C_5 petroleum resin, prepared a new diesel oil pour point depression.
通过在C5石油树脂分子上接枝引入极性基团得到的接枝物(MAHC5)与EVA树脂进行共聚反应制得了一种新型柴油降凝剂,探讨了反应温度、反应时间、引发剂用量、共聚物种类及用量对降凝剂粘度与降凝效果的影响。
2.
C_5 petroleum resin was modified with malefic anhydride as the modifier and DCP as the initiator.
以马来酸酐为改性剂、过氧化二异丙苯为引发剂对C5石油树脂进行改性。
5) C 5 petroleum resin
C5石油树脂
1.
A new EVA hot melt adhsive was prepared with maleic anhydide modified C 5 petroleum resin (MAH-C 5 ) as tackifier, and the influences were discussed including the kinds of EVA, the dosages of MAH-C 5 and paraffin.
以马来酐改性C5石油树脂 (MAH—C5)作增粘剂 ,制备了新型的EVA(聚乙烯 醋酸乙烯 )热熔胶 ,讨论了EVA种类、MAH—C5与石蜡用量对该热熔胶性能的影响。
6) piperylene C5 petroleum resin
间戊二烯C5石油树脂
1.
Investigation of piperylene C5 petroleum resin hydrogenation upgrading process
间戊二烯C5石油树脂加氢改质工艺研究
2.
Investigation of modified piperylene C5 petroleum resin used as pour point depressant for diesel oil
间戊二烯C5石油树脂改性作为柴油降凝剂的研究
补充资料：石油树脂
烃类裂解的液态产物中，经除去苯、甲苯、二甲苯后,所余重质芳烃和烯烃混合物,在催化剂作用下，聚合生成的一种合成树脂。聚合催化剂通常用三氯化铝、氟化硼或硫酸(见酸碱催化剂)，聚合温度0～100℃。根据聚合条件的不同，生成的石油树脂具有不同软化点，自粘稠状至固态不等，颜色自浅黄、琥珀色到黑色，相对密度(15℃)0.98～1.06，折光指数1.53～1.60。石油树脂有憎水性，与合成橡胶及其他合成树脂有良好的混溶性，软化点为30～60℃的石油树脂用作合成橡胶、天然橡胶的增粘剂、也作胶粘剂;软化点为60～130℃的石油树脂，用作印刷用油墨的增量剂和涂料的改性剂（增加涂料的硬度、耐水性和附着力），还可用作纸张的胶料、防水布的防水剂等。石油树脂的原料较丰富，生产成本低廉，用途广泛。