1) C5 resin
C5树脂
2) C5 Petroleum Resin
C5石油树脂
1.
C5 petroleum resin applied in road marking;
C5石油树脂在路标漆中的应用
2.
Hydrogenated C5 petroleum resin was prepared with C5 petroleum resins as feedstock at 240～270℃,14～17MPa,liquid space velocity 0.
以C5石油树脂为原料,在温度为240~270℃,压力为14~17 MPa,液体空速为0。
3.
The polymerization processes of C5 petroleum resin were reviewed,the applications of C5 petroleum resin in many fields such as adhesive,coating,paint,printing ink and color asphalt wered studied,and some advice was given to the petroleum resin factories.
介绍了C5石油树脂聚合工艺,研究了C5石油树脂在胶粘剂、涂料、油漆、油墨及彩色沥青等领域的应用,并对国内石油树脂生产企业提出一些建议。
3) C_5 petroleum resin
C5石油树脂
1.
Used C_5 petroleum resin as the materials, through graft reaction, the polar groups was added onto the molecular of C_5 petroleum resin, prepared a new diesel oil pour point depression.
通过在C5石油树脂分子上接枝引入极性基团得到的接枝物(MAHC5)与EVA树脂进行共聚反应制得了一种新型柴油降凝剂,探讨了反应温度、反应时间、引发剂用量、共聚物种类及用量对降凝剂粘度与降凝效果的影响。
2.
C_5 petroleum resin was modified with malefic anhydride as the modifier and DCP as the initiator.
以马来酸酐为改性剂、过氧化二异丙苯为引发剂对C5石油树脂进行改性。
4) C 5 petroleum resin
C5石油树脂
1.
A new EVA hot melt adhsive was prepared with maleic anhydide modified C 5 petroleum resin (MAH-C 5 ) as tackifier, and the influences were discussed including the kinds of EVA, the dosages of MAH-C 5 and paraffin.
以马来酐改性C5石油树脂 (MAH—C5)作增粘剂 ,制备了新型的EVA(聚乙烯 醋酸乙烯 )热熔胶 ,讨论了EVA种类、MAH—C5与石蜡用量对该热熔胶性能的影响。
5) hydrogenated C5 petroleum resin
加氢C5石油树脂
1.
The compatibility of styrene-butadiene-styrene block copolymer(SBS)with hydrogenated C5 petroleum resin(HC5R)was studied by dynamic mechanical analysis.
通过动态力学分析研究了苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)与加氢C5石油树脂(HC5R)共混体系的相容性,并考察了臭氧处理对共混体系的影响。
6) C5 hydrogenation petroleum resin
C5加氢石油树脂
1.
Based on the behavior of self-polymerization of active components during the production of C5 hydrogenation petroleum resin,a compound inhibitor(inhibitor and dispersant) was added in the pretreatment process of raw materials.
针对C5加氢石油树脂生产过程中存在的活性组分自聚现象,在原料预处理工序中加入复合型阻聚剂(阻聚剂和分散剂)。
补充资料：C5树脂
分子式：
CAS号：
性质：丁烷下脚油是石油深度裂化后的副产物，其主要组分为C5脂肪族烯烃，如间戊二烯、异戊二烯、环戊二烯等。这些烯烃经聚合便得C5树脂。这是一类热塑性树脂，色浅，高度不饱和，易溶于烃类溶剂中，与其他树脂的混溶性好，广泛用于涂料工业。配制成漆后，其涂膜的耐水性、耐酸碱性甚好。
CAS号：
性质：丁烷下脚油是石油深度裂化后的副产物，其主要组分为C5脂肪族烯烃，如间戊二烯、异戊二烯、环戊二烯等。这些烯烃经聚合便得C5树脂。这是一类热塑性树脂，色浅，高度不饱和，易溶于烃类溶剂中，与其他树脂的混溶性好，广泛用于涂料工业。配制成漆后，其涂膜的耐水性、耐酸碱性甚好。