1) blowhole shrinkage
气缩孔
1.
The defects of blowhole shrinkage and boiling often occurr in the production of cast steel bracket,and the process yield is low,the core cost is high.
支架类铸钢件在生产过程中存在气缩孔和呛火,且工艺出品率低,芯子成本高。
2) gas and shrinkage porosity
气孔及缩孔
3) Porosity check
气缩孔检测
4) shrinkhole
缩孔，气沟砂眼
5) shrinkage porosity
收缩气孔巢(铸疵)
6) shrinkage hole
缩孔
1.
Numerical Simulation for Shrinkage Hole (Porosity) Formation in TiAl Alloy Product in Investment Casting;
TiAl合金熔模精铸件缩孔形成的数值模拟及预测
2.
The Ways for Elimination of Shrinkage Hole in Light Casting with Isolated Hot Spot;
有孤立热节的小铸件缩孔解决方法
3.
By this way,we can be sure of not bring out shrinkage holes and shrinkage porosities during the activity of new products developing and quality improvement,the good castings with nigh quality have been obtained.
采用不同铸造工艺方案,根据其存在的问题,通过分析产生的原因,利用“铸造过程模拟优化集成系统软件CASTsoft精铸CAE软件,”对浇注系统进行模拟分析,在新产品开发和质量改进活动中,保证在生产实践中避免缩孔和缩松缺陷,不断改进工艺,获得了优质铸件。
补充资料：防缩孔剂
分子式：
CAS号：
性质： 用于防止涂膜上形成不规则的、有如碗状的、小的凹陷的弊病，使涂膜趋于平整的助剂。缩孔又称为坑口、火山口、弹坑。缩孔形成的关键是涂膜表面产生了表面张力梯度。防缩孔剂的实质是改善涂料的流平性。所用品种参见流平剂。
CAS号：
性质： 用于防止涂膜上形成不规则的、有如碗状的、小的凹陷的弊病，使涂膜趋于平整的助剂。缩孔又称为坑口、火山口、弹坑。缩孔形成的关键是涂膜表面产生了表面张力梯度。防缩孔剂的实质是改善涂料的流平性。所用品种参见流平剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。