1) slurry infiltration
料浆浸渗法
1.
In order to introduce a mass of SiC fillers into 10mm thick 3-D carbon fiber perform,four slurry infiltration method were applied: vacuum infiltration,pressure infiltration,pressure filtration,and vacuum suction straining.
为了在厚度为10mm的3D碳纤维预制体中大量引入SiC微粉,在料浆不变的基础上采用真空浸渗法、加压浸渗法、加压过滤法、真空吸滤法等四种料浆浸渗法进行试验,并对引入微粉的量及其分布进行分析对比。
2) slurry application
浆料浸涂法
1.
Then for the first time, the SiC-Yb2SiO5 intermediate coat was applied on the SiC coated Cf/SiC composites through PCS-SiC-Yb2SiO5 slurry application.
用溶胶凝胶法制备粒径为200～300nm的单相Yb2SiO5粉体,然后用PCS-SiC-Yb2SiO5浆料浸涂法制备SiC-Yb2SiO5过渡层,因PCS粘结强度大,且热解后能在原位生成SiC,故能大大增加涂层的结合力。
3) slurry pack cementation
浆料包渗法
4) wet material combined with cement grout
潮料渗浆法
5) preimpregnation of pulp
浆料预浸
6) slurry
[英]['slʌri] [美]['slɝɪ]
浸渍浆料
1.
It is pointed that the composites infiltrated with the slurry of PCS/cross-linking agent had a density of 1.
采用先驱体转化法,以聚碳硅烷/二甲苯、聚碳硅烷/二甲苯/碳化硅粉、聚碳硅烷/交联剂三种浆料体系分别浸渍增强体,裂解制备Cf/SiC复合材料,考察了浸渍浆料体系对Cf/SiC复合材料的结构和性能的影响。
补充资料：热浸渗铝镀层
分子式：
CAS号：
性质：用热浸镀方法在钢表面形成的镀铝层。钢件浸入700～730℃的熔融铝液中，表面生成铝铁化合物，同时一部分铝原子渗入钢铁基体形成扩散层。为使镀层与基体金属牢固结合，一般在热浸后还要进行一次900～980℃的高温处理，使镀层软熔扩散，形成合金层。镀层具有优良的耐大气腐蚀性、抗高温氧化性和抗高温硫腐蚀性能。在石油、化工、能源、海洋工程等领域广泛应用。
CAS号：
性质：用热浸镀方法在钢表面形成的镀铝层。钢件浸入700～730℃的熔融铝液中，表面生成铝铁化合物，同时一部分铝原子渗入钢铁基体形成扩散层。为使镀层与基体金属牢固结合，一般在热浸后还要进行一次900～980℃的高温处理，使镀层软熔扩散，形成合金层。镀层具有优良的耐大气腐蚀性、抗高温氧化性和抗高温硫腐蚀性能。在石油、化工、能源、海洋工程等领域广泛应用。