1) Dynamic mixing
动态混炼
1.
The techniques and equipments of the dynamic extrusion,dynamic injection and dynamic mixing implemented by the application of vibration to the polymer processings were introduced.
本文简要介绍了振动力场作用下,动态挤出成型过程中的动态固体输送、动态熔融塑化、动态熔体输送过程的机理及实验研究,分析了脉动压力对注射过程的影响,以及动态混炼过程中强制混炼、强制分散的原理。
2.
HDPE/Mg(OH)2 was made out of tri-screw dynamic mixing extruder,which is combined with the electromagnetic vibration technology.
将电磁振动技术和三螺杆挤出机结合起来,用三螺杆动态混炼挤出机挤出HDPE/Mg(OH)2,通过对挤出物料中Mg(OH)2的分散性研究,得出三螺杆动态混炼对Mg(OH)2的分散性和HDPE/Mg(OH)2力学性能的影响规律,并对在不同振动参数(振幅、频率)下制取标准力学性能测试试样与稳态挤出时试样力学性能的比较获取最优的振动参数范围,解决了因Mg(OH)2填充量过高而严重影响复合材料力学性能的问题。
2) dynamical plasticizing
动态塑化混炼
3) tri-screw dynamic mixing extruders
三螺杆动态混炼挤出机
1.
Vibration force field was introduced into processing of plastics in tri-screw dynamic mixing extruders,so as to intensifying mixability and dispersion.
三螺杆动态混炼挤出机将振动力场引入到物料的塑化混炼挤出过程,达到强化混炼和分散的目的。
4) Electromagnetic dynamic mixing extrusion of plastics
电磁动态塑料混炼挤出
5) dynamic steelmaking
动态炼钢
补充资料：密炼机混炼
分子式：
CAS号：
性质： 现代橡胶工厂主要采用密胶机混炼。与开炼机相比，密炼机生产能力大，混炼时间短，生产效率高，操作安全，劳动量小。密炼机混炼的关键是控制好混炼温度，由于密炼机转速快（20～40r/min），胶料受剪切力与摩擦力很大，升温快，一般混炼排胶温度宜控制在100～130℃。密炼机混炼有一段混炼法和两段混炼法。一段混炼法是将生胶与配合剂分批加料，炼好后排胶，也可留少部分生胶及硫化剂在最后加入，混炼至排胶。两段混炼法是先用高速高压密炼机炼成生胶加炭黑和软化剂之类的母炼胶，排胶压片停放冷却后，再以低速密炼机或压片机加硫黄和促进剂完成混炼。两段混炼法的优点是显著提高混炼的均匀性，即提高硫化胶的物理性能，两段间的冷却可避免胶料焦烧，又可缩短混炼时间，提高生产效率。
CAS号：
性质： 现代橡胶工厂主要采用密胶机混炼。与开炼机相比，密炼机生产能力大，混炼时间短，生产效率高，操作安全，劳动量小。密炼机混炼的关键是控制好混炼温度，由于密炼机转速快（20～40r/min），胶料受剪切力与摩擦力很大，升温快，一般混炼排胶温度宜控制在100～130℃。密炼机混炼有一段混炼法和两段混炼法。一段混炼法是将生胶与配合剂分批加料，炼好后排胶，也可留少部分生胶及硫化剂在最后加入，混炼至排胶。两段混炼法是先用高速高压密炼机炼成生胶加炭黑和软化剂之类的母炼胶，排胶压片停放冷却后，再以低速密炼机或压片机加硫黄和促进剂完成混炼。两段混炼法的优点是显著提高混炼的均匀性，即提高硫化胶的物理性能，两段间的冷却可避免胶料焦烧，又可缩短混炼时间，提高生产效率。