1) low temperature solid boronizing
低温固体渗硼
1.
The boronizing agent, selection of steel, pre-treatment, microstructure and property in low temperature solid boronizing were described.
对低温渗硼过程中的渗硼剂、选择用钢、预处理及组织性能等方面的研究进展进行了阐述,给出了各自的最佳适用范围,并对低温固体渗硼的发展前景做出了展望。
2) low temperature pack boro carbo nitriding
低温固体硼-碳-氮共渗
3) low-temperature boronizing
低温渗硼
4) pack boronizing
固体渗硼
1.
Three different pack box techniques, which change the contacts between samples and boronizing agent, were designed to investigate how the activated boron atoms are transferred onto the sample surface during pack boronizing.
设计了 3种不同的装罐方法 ,通过改变试样与渗剂的接触方式 ,对固体渗硼时渗剂中活性硼原子输运到试样表面的方式进行了研究。
2.
Different pack boronizing heat treatment processes are designed and the microstructures and the mechanical properties are examined for 5CrNiMo steel samples.
对 5CrNiMo钢试样进行了固体渗硼热处理工艺试验、组织观察与力学性能测定 ,确定了提高 5CrNiMo钢制热锻模服役寿命的固体渗硼热处理工艺 ,并用于实际生产。
3.
In this paper,the effects of urea on pack boronizing have been studied.
研究了尿素对固体渗硼的作用。
5) solid boronizing
固体渗硼
1.
A process of solid boronizing and laser surface modification was applied to get boron eutectic layer for lowering its brittleness and improving its wear resistance.
采用固体渗硼 +激光表面处理的复合热处理工艺 ,使表层得到共晶型硼化物以期降低渗硼层脆性 ,提高其耐磨性。
6) solid boriding
固体渗硼
1.
With the fundamentals of electrocemical reation, an electric field was applied to solid boriding device, so that a corrosive battery was formed in the boriding process.
本文应用电化学反应的基本原理，在固体渗硼装置中外接电场，使之构成腐蚀电池。
补充资料：低温离子渗硫
低温离子渗硫
精密离子均匀轰击
1、低温离子渗硫
在 20 世纪八十年代，材料物理学家张弋飞在世界上首先发现，固体硫蒸气产生辉光放电的效应，该效应使金属零件在低温下形成固体润滑层—渗硫层。 这就是著名的“低温离子渗硫”，它的全称是金属表面形成硫化物层的方法和设备，获得了 中、英、德、法、瑞、意、日等多国专利。
至1997年底，低温离子渗硫专利普通许可21家企业生产，取得广泛的经济效益和社会效益。
国内一些企业和科研单位声称开发出“离子渗硫”、“离子硫化”、“真空等离子渗硫”，或称“国外引进”；三家企业被北京市中院判决侵权，一家被宣告实用新型专利无效；见侵权维权
实际上，离子渗硫只有一个能达到120微米渗层深度发明专利，，即“金属表面形成硫化物层的方法和设备”专利。