1) powder boron nitriding
固体硼氮复合渗
2) Boronitriding
硼氮复合渗
1.
Boronitriding used in valve core to improve corrosion resistance;
采用硼氮复合渗提高阀芯耐蚀性能
3) pack boronitriding
固体硼氮共渗
1.
The boronitriding medium,process paramaters,microstructures and properties of case,application on dies of pack boronitriding are studied in this paper.
研究了固体硼氮共渗技术的渗剂、工艺参数、共渗后的组织与性能及其在模具上的应用。
4) Nitro-carbon-boronizing
硼氮碳复合渗
5) pack boronizing
固体渗硼
1.
Three different pack box techniques, which change the contacts between samples and boronizing agent, were designed to investigate how the activated boron atoms are transferred onto the sample surface during pack boronizing.
设计了 3种不同的装罐方法 ,通过改变试样与渗剂的接触方式 ,对固体渗硼时渗剂中活性硼原子输运到试样表面的方式进行了研究。
2.
Different pack boronizing heat treatment processes are designed and the microstructures and the mechanical properties are examined for 5CrNiMo steel samples.
对 5CrNiMo钢试样进行了固体渗硼热处理工艺试验、组织观察与力学性能测定 ,确定了提高 5CrNiMo钢制热锻模服役寿命的固体渗硼热处理工艺 ,并用于实际生产。
3.
In this paper,the effects of urea on pack boronizing have been studied.
研究了尿素对固体渗硼的作用。
6) solid boronizing
固体渗硼
1.
A process of solid boronizing and laser surface modification was applied to get boron eutectic layer for lowering its brittleness and improving its wear resistance.
采用固体渗硼 +激光表面处理的复合热处理工艺 ,使表层得到共晶型硼化物以期降低渗硼层脆性 ,提高其耐磨性。
补充资料：碳氮硼三元共渗
分子式：
CAS号：
性质：碳氮硼三元共渗是使钢制工件同时渗入碳、氮、硼三种元素的化学热处理工艺。共渗后渗层的硬度较渗硼为低(HV600～1000)。碳氮硼三元共渗如用于石油机械易损零件，能提高使用寿命。碳氮硼三元共渗后空冷即可得到HV750的硬度，对于上述钢材制造的薄小工件，可以省去淬火工序。碳氮硼三元共渗也可以在气体介质中进行，例如用尿素(2500g)、甲醇(8L)、硼酸三甲酯(5L)、丙酮(6L)的混合渗剂滴入840~860℃的井式渗碳炉中，保温3～5h后，在低碳合金渗碳钢上可得到0.4～0.6mm渗层，表面硬度达HRC63～65，甚至更高。
CAS号：
性质：碳氮硼三元共渗是使钢制工件同时渗入碳、氮、硼三种元素的化学热处理工艺。共渗后渗层的硬度较渗硼为低(HV600～1000)。碳氮硼三元共渗如用于石油机械易损零件，能提高使用寿命。碳氮硼三元共渗后空冷即可得到HV750的硬度，对于上述钢材制造的薄小工件，可以省去淬火工序。碳氮硼三元共渗也可以在气体介质中进行，例如用尿素(2500g)、甲醇(8L)、硼酸三甲酯(5L)、丙酮(6L)的混合渗剂滴入840~860℃的井式渗碳炉中，保温3～5h后，在低碳合金渗碳钢上可得到0.4～0.6mm渗层，表面硬度达HRC63～65，甚至更高。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。