1) 82B steel wire coil
82B钢盘条
2) 82B wire rod
82B盘条
1.
It is pointed out that there is little difference between homemade 82B wire rod and import in the aspect of chemical component,physical and chemical property and content of inclusion,uniformity in whole wire rod and the stability need further raising.
介绍国产盘条生产桥梁缆索用镀锌钢丝的工艺技术、制造过程,分析研究有关技术要点,指出国产82B盘条的化学成分、理化性能及夹杂物含量与进口盘条相差不大,通条性和稳定性有待进一步提高。
2.
To observe the microstructure of 82B wire rod.
观察82B盘条的组织,发现异常组织(马氏体、网状渗碳体)在拉拔时造成纤维裂纹,夹杂物不造成纤维裂纹,异常组织超过一定的尺寸会造成拉拔断丝,提出消除或减轻82B盘条异常组织的建议。
3.
On the basis of break cause of 82B wire rod during wire drawing,break comprises such three kinds as materialbreak,welding break and process break.
根据82B盘条在拉拔过程中造成断裂的原因,将断裂分为材质断裂、焊接断裂和工艺断裂3类。
3) 82B steel
82B钢
1.
Optimization research on process condition for 82B steel based on neural network and particle swarm optimizing algorithm;
基于神经网络与粒子群优化算法的82B钢工艺条件的优化研究
2.
The oxide inclusions in 82B steel is mainly generated in process of deoxidation,second oxidation,slag entrament,and refractory line corradation.
82B钢中氧化物系夹杂物的来源主要是脱氧产物和钢的二次氧化、卷渣及耐火材料内衬侵蚀。
3.
The 82B steel is produced at JISCO by hot metal pretreatment→50 t top blown converter→LF refining →continuous casting billet→controlled rolling & cooling process.
生产统计结果表明,82B钢中平均氧含量为30×10-6,氮含量45×10-6,氢含量1。
5) high carbon steel 82B
高碳钢82B
1.
Controlling nitrogen in refining high carbon steel 82B
高碳钢82B精炼过程中的氮控制
6) 80 steel wire rod
80钢盘条
1.
To introduce production process flow and mechanical properties of high strength 80 steel wire rod.
介绍高强度80钢盘条的生产工艺流程和力学性能指标,通过金相组织分析,指出钢的组织中出现网状渗碳体是拉拔断裂的主要原因,采用人工时效并改进拉拔工艺,使各道次的压缩率均匀合理,在一定程度上可以弥补组织不当带来的缺陷,有利于盘条的拉拔。
2.
By means of microstructure test,chemical composition analysis,fracture test,inclusion spectrum analysis of 80 steel wire rod with lower strength and bigger plasticity variety,the results show that the cause of lower strength is lower content of sorbite and the reasons for bigger plasticity variety are meshy carbides and big grain brittle inclusions inside the wire rod.
通过对强度偏低、塑性变化较大的80钢盘条的金相检验、化学成分分析、断口检验、夹杂物能谱分析,认为其强度偏低的原因是索氏体含量偏低,塑性变化较大的原因是盘条内部存在网状碳化物和大颗粒脆性夹杂物。
补充资料：前南斯拉夫m82/m82a式5.56mm轻机枪
Image:11628983310860368.jpg
前南斯拉夫m82/m82a式5.56mm轻机枪
概 述
ｍ８２式和ｍ８２ａ式５．５６ｍｍ轻机枪与ｍ８０式和ｍ８０ａ式步枪构成前南斯拉夫的５．５６ｍｍ枪族。ｍ８２式和ｍ８２ａ式是从ｍ７２式轻机枪演变而来的，主要用于出口。
结构特点
１．枪ｍ８２式和ｍ８２ａ式枪采用前苏联卡拉什尼柯夫步枪的导气式工作原理，闭锁机构为枪机回转式，用３０发可卸弹匣供弹。该枪有一个专门设计的气体调节器，即使在某些情况下将不同能量水平的弹药装入弹匣，也能保证操作无误。枪上配有两脚架和提把，ｍ８２式为固定式木制枪托，ｍ８２ａ式为上下折叠的金属枪托。２．瞄准装置该枪采用可调表尺的缺口式照门。３.弹药该枪发射美国ｍ１９３式或北约ｓｓ１０９式５．５６ｍｍ枪弹。
性能数据
口径----５．５６ｍｍ
初速----１０００ｍ／ｓ
有效射程----４００ｍ
自动方式----导气式
闭锁方式----枪机回转式
发射方式----单发、连发
供弹方式----弹匣
容弹量----３０发
全枪长----１０２０ｍｍ
枪管长----５４２ｍｍ
膛线----６条，右旋，缠距１７８ｍｍ
全枪质量(不含弹匣)----4kg
瞄准基线长----49８ｍｍ
配用弹种----m193式或ss109式5.56×45,mm枪弹
说明：补充资料仅用于学习参考，请勿用于其它任何用途。