1) 75 # coil rod
75#钢盘条
2) 80 steel wire rod
80钢盘条
1.
To introduce production process flow and mechanical properties of high strength 80 steel wire rod.
介绍高强度80钢盘条的生产工艺流程和力学性能指标,通过金相组织分析,指出钢的组织中出现网状渗碳体是拉拔断裂的主要原因,采用人工时效并改进拉拔工艺,使各道次的压缩率均匀合理,在一定程度上可以弥补组织不当带来的缺陷,有利于盘条的拉拔。
2.
By means of microstructure test,chemical composition analysis,fracture test,inclusion spectrum analysis of 80 steel wire rod with lower strength and bigger plasticity variety,the results show that the cause of lower strength is lower content of sorbite and the reasons for bigger plasticity variety are meshy carbides and big grain brittle inclusions inside the wire rod.
通过对强度偏低、塑性变化较大的80钢盘条的金相检验、化学成分分析、断口检验、夹杂物能谱分析,认为其强度偏低的原因是索氏体含量偏低,塑性变化较大的原因是盘条内部存在网状碳化物和大颗粒脆性夹杂物。
3) 70 steel wire rod
70钢盘条
1.
The 70 steel wire rod is came into fracture during drawing.
70钢盘条在拉拔时发生断裂,经对盘条拉拔工艺和盘条材质进行分析,认为盘条心部存在网状渗碳体是造成拉拔断裂主要原因。
4) 82B steel wire coil
82B钢盘条
6) MD rod coil
MD钢盘条
补充资料：selenium-75 75Se
分子式：
CAS号：
性质：质量数为75的硒的放射性核素。半衰期120.4天。以电子俘获方式进行核衰变，伴随的γ射线能量复杂，主要为0.265MeV。可从反应堆中以中子轰击74Se而制得。临床上用于胰腺及甲状腺扫描。
CAS号：
性质：质量数为75的硒的放射性核素。半衰期120.4天。以电子俘获方式进行核衰变，伴随的γ射线能量复杂，主要为0.265MeV。可从反应堆中以中子轰击74Se而制得。临床上用于胰腺及甲状腺扫描。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条