1) sol-gel-dipping process
溶胶-凝胶-浸渍提拉法
1.
With thiourea as the source substance of S,with Titanium tetrabutoxide(Ti(OC4H9)4 as the precursor of titanium dioxide and with honeycomb ceramics as carriers,S-TiO2 films were prepared by a modified sol-gel-dipping process.
以硫脲为S的源物质,以钛酸丁酯为TiO2的前驱体,以蜂窝陶瓷为载体,采用改进的溶胶-凝胶-浸渍提拉法制备Ti1-xSxO2薄膜,探讨热处理温度、S掺杂量及涂膜等工艺条件对Ti1-xSxO2薄膜的光催化活性的影响。
2) sol-dip-coating method
溶胶浸渍提拉法
1.
In this study, tungsten trioxide EC films were successfully prepared via sol-dip-coating method and sol-electrophoretic method using stable tungsten trioxide sol synthesized by tungstic acid.
溶胶浸渍提拉法制备的氧化钨薄膜,在500℃保温3h的热处理温度下表面非常平整,形成了纳米尺度的晶粒,薄膜具有较好的着色-褪色性能,薄膜的循环伏安特性稳定,离子的注入与抽出过程可逆性好,薄膜的着色态与褪色态的最大透光率差值出现在750nm波长处,约为45%,具有较好的光线调节能力。
3) sol-gel-impregnation method
溶胶-凝胶浸渍法
4) sol gel immersion method
溶胶-凝胶-浸渍法
5) sol-gel-immersion method
溶胶-凝胶法-浸渍法
6) sol-gel-dip
溶胶凝胶浸渍
1.
Using tetrabutyl titanate and granular activated carbon as the raw material, nanometer-sized TiO_ 2 photocatalyst immobilized on activated carbon(TiO_ 2/AC)was prepared by sol-gel-dip method.
以钛酸四丁酯和粒状活性炭(AC)为主要原料,采用溶胶凝胶浸渍法制备出负载型纳米TiO2/AC催化剂。
补充资料：溶胶-凝胶法
分子式：
CAS号：
性质：一种用于制取无机固体材料和器件的方法。无机固体化合物和无机材料通常是利用高温固相反应制备，但是，一般地说，高温固相反应得到固体产物的均匀性较差，反应所需的温度较高，产物的料理论基础和形貌也无法控制。溶胶-凝胶方法利用前体物（如醇盐或无机盐）将反应物在分子的尺度上均匀混合，经溶胶和凝胶过程使之转变为固体；由于固体凝胶中反应物是在分子水平上均匀混合，避免了固相反应扩散过程，使反应可以在较低的温度下进行，还可以根据需要将凝胶成型，再经热处理得到具有一定形状的材料和器件。利用溶胶-凝胶方法可以制备出各种形态的材料，如薄膜、纤维、块体或粉末等。近年来，溶胶-凝胶方法在很多领域中得到了广泛应用，特别是在陶瓷材料和器件上制造中的应用，得到了多种均匀、具有特定微结构和性能的固体材料。
CAS号：
性质：一种用于制取无机固体材料和器件的方法。无机固体化合物和无机材料通常是利用高温固相反应制备，但是，一般地说，高温固相反应得到固体产物的均匀性较差，反应所需的温度较高，产物的料理论基础和形貌也无法控制。溶胶-凝胶方法利用前体物（如醇盐或无机盐）将反应物在分子的尺度上均匀混合，经溶胶和凝胶过程使之转变为固体；由于固体凝胶中反应物是在分子水平上均匀混合，避免了固相反应扩散过程，使反应可以在较低的温度下进行，还可以根据需要将凝胶成型，再经热处理得到具有一定形状的材料和器件。利用溶胶-凝胶方法可以制备出各种形态的材料，如薄膜、纤维、块体或粉末等。近年来，溶胶-凝胶方法在很多领域中得到了广泛应用，特别是在陶瓷材料和器件上制造中的应用，得到了多种均匀、具有特定微结构和性能的固体材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条