1) sol-dipping method
溶胶-浸渍法
1.
The reaction kinetics and mechanism of oxidation reaction of SiO_2 coating/3-D braided carbon fiber prepared by the sol-dipping method were studied systemly through XRD,SEM,isothermal weight-loss and non-isothermal TG-DTG methods.
采用溶胶-浸渍法,在三维碳纤维编织体的纤维表面涂覆SiO2涂层,通过XRD、SEM、等温氧化失重和非等温TG-DTG等测试手段研究了制备方法对涂层完整性的影响,并对涂层/编织体材料(CB)氧化反应的动力学和机理进行了系统研究。
2.
The SiO2 coating on 3-D braided carbon fiber was prepared by the sol-dipping method.
采用溶胶-浸渍法,成功地在三维编织碳纤维的纤维表面涂覆SiO2,并通过碳热还原反应制得厚度约为0。
3.
The SiO2 coating on 3-D carbon fiber braids was prepared by the sol-dipping method.
采用溶胶-浸渍法,在三维碳纤维编织体的纤维表面涂覆SiO_2涂层。
2) sol-gel-impregnation method
溶胶-凝胶浸渍法
3) sol gel immersion method
溶胶-凝胶-浸渍法
4) e-sol-dipping method
类溶胶-浸渍法
5) sol-dipping template method
溶胶-浸渍模板法
6) sol-dip-coating method
溶胶浸渍提拉法
1.
In this study, tungsten trioxide EC films were successfully prepared via sol-dip-coating method and sol-electrophoretic method using stable tungsten trioxide sol synthesized by tungstic acid.
溶胶浸渍提拉法制备的氧化钨薄膜,在500℃保温3h的热处理温度下表面非常平整,形成了纳米尺度的晶粒,薄膜具有较好的着色-褪色性能,薄膜的循环伏安特性稳定,离子的注入与抽出过程可逆性好,薄膜的着色态与褪色态的最大透光率差值出现在750nm波长处,约为45%,具有较好的光线调节能力。
补充资料：固体物料浸渍法
分子式：
CAS号：
性质：采用熔融金属、液态润滑剂或其他液态非金属物质来浸渍多孔骨架状固体的方法。该法基于毛细管渗透原理。可分为全浸法，部分浸入法，表面接触法等。还可采用液压，离心力，抽真空等措施增加渗透的附加压力。这种工艺已被广泛应用于许多领域。如多晶氧化铝自润滑含油轴承(将烧好的多晶轴承浸入油中)、金属陶瓷无油润滑活塞环(金属陶瓷浸渍于液态塑料中)、钨渗铜的喷管材料、用熔融的镍、钴、铁浸渍的钨与碳化钛工具和模具材料等。
CAS号：
性质：采用熔融金属、液态润滑剂或其他液态非金属物质来浸渍多孔骨架状固体的方法。该法基于毛细管渗透原理。可分为全浸法，部分浸入法，表面接触法等。还可采用液压，离心力，抽真空等措施增加渗透的附加压力。这种工艺已被广泛应用于许多领域。如多晶氧化铝自润滑含油轴承(将烧好的多晶轴承浸入油中)、金属陶瓷无油润滑活塞环(金属陶瓷浸渍于液态塑料中)、钨渗铜的喷管材料、用熔融的镍、钴、铁浸渍的钨与碳化钛工具和模具材料等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条