1) Yb:GdAlO3
Yb:GdAlO3
1.
Nanoscaled powders Nd∶GdAlO3(5at%) and Yb∶GdAlO3(5at%) were synthesized by co-precipitation method with Gd2O3,Al(NO3)3·9H2O,Nd2O3 and Yb2O3 as the starting materials and aqueous ammonia as precipitator.
9H2O、Nd2O3(Yb2O3)为原料、氨水为沉淀剂,合成了Nd∶GdAlO3(5%(原子分数))和Yb∶GdAlO3(5%(原子分数))纳米多晶粉末,采用X射线衍射(XRD)和Rietveld精修方法对晶体结构进行了研究,采用场发射扫描电镜(FESEM)对晶体的形貌进行了研究,同时对晶体的发射光谱进行了测量。
2) Yb
Yb
1.
MICROSTRUCTURES AND MECHANICAL PROPERTIES OF AS-CAST Mg-xYb AND Mg-xYb-0.4Zr ALLOYS;
Mg-xYb和Mg-xYb-0.4Zr合金的铸态组织及力学性能
2.
Study on Growth and Cracking of Cr,Yb,Ho:YAGG Tunable Laser Crystal;
Cr,Yb,Ho:YAGG可调谐激光晶体生长及开裂研究
3.
Synthesis of High Luminescent Y_2O_3∶Er,Yb Upconversion Nanocrystals;
高发光强度上转换材料Y_2O_3∶Er,Yb纳米晶的制备
3) Yb(Ⅲ)
Yb(Ⅲ)
4) Yb:KYW crystal
Yb:KYW
5) Yb:Y2O3
Yb:Y2O3
1.
Er,Yb∶Y2O3 laser ceramics precursor was synthesized by sol-gel method with Y2O3,Yb2O3 and Er2O3,and the pH value of the solution was 3~4.
以Y2O3,Yb2O3和Er2O3为原料,控制溶液的pH值为3~4左右,采用柠檬酸溶胶-凝胶法制备出Er,Yb∶Y2O3倍半氧化物激光陶瓷前驱粉体。
6) Yb:BaWO_4
Yb:BaWO4
1.
The polycrystalline of Yb∶BaWO_4 had been synthesized by the way of liquid-phase reaction, and then the colorless and uncracked Yb∶BaWO_4 crystal was grown using Czochralski method.
采用液相法合成掺镱钨酸钡(Yb∶BaWO4)晶体的原料,并用Czochralski法(提拉法)生长出无色透明不开裂的Yb∶BaWO4晶体。
参考词条
Yb:glass
NaYF4:Yb
La/Yb
NF-YB
Yb:YAG
Y/Yb-Sr/Y-La/Yb
Er:Yb(Ho:Yb)共掺杂
Yb:(Lu,Gd)VO4
Yb:GdVO_4晶体
Yb:YAG晶体
掺Yb玻璃
Yb-Co合金
Yb:YPxV1-xO4晶体
Yb α-SiAION
Yb(OTf)_3
Al2O3/NaOH
三碘甲状腺原氨酸/针灸效应
补充资料:4-[4-[[3-[(ethylphenylamino)sulfonyl]-4-methylphenyl]azo]-4,5-dihydro-3-methyl-5-oxo-1H-pyrazol-1-yBenzenesulfonic acid
CAS:83006-48-8
中文名称:4-[4-[[3-[(乙基苯基氨基)磺酰基]-4-甲基苯基]偶氮]-4,5-二氢-3-甲基-5-氧-1H-吡唑-1-基]苯磺酸
英文名称:4-[4-[[3-[(ethylphenylamino)sulfonyl]-4-methylphenyl]azo]-4,5-dihydro-3-methyl-5-oxo-1H-pyrazol-1-yBenzenesulfonic acid
中文名称:4-[4-[[3-[(乙基苯基氨基)磺酰基]-4-甲基苯基]偶氮]-4,5-二氢-3-甲基-5-氧-1H-吡唑-1-基]苯磺酸
英文名称:4-[4-[[3-[(ethylphenylamino)sulfonyl]-4-methylphenyl]azo]-4,5-dihydro-3-methyl-5-oxo-1H-pyrazol-1-yBenzenesulfonic acid
说明:补充资料仅用于学习参考,请勿用于其它任何用途。