1)  Yb:YAG crystal
Yb:YAG晶体
1.
The segregation coefficient of Yb 3+ ions in TGT-grown Yb∶YAG crystals determined by ICP-AES method is equal to 1.
应用温梯法生长出直径为 76mm的Yb∶YAG晶体。
2.
We have performed the study of defects in Yb∶YAG crystal grown by CZ method by means of transmission synchrotron topography and optical birefringence topography.
用同步辐射透射白光形貌相和应力双折射法研究了沿 111 方向生长的Yb∶YAG晶体的生长缺陷、晶体中的位错起源和走向。
3.
An Yb∶YAG disk with the dimension of Φ10 mm×300 μm and the doping concentration of 10%(atomic fraction) was mounted onto the copper heat sink with an indium foil and the temperature of Yb∶YAG crystal was controlled by a water-cooled system.
选用掺杂原子数分数为10%,几何尺寸为Φ10 mm×300μm的薄片状Yb∶YAG晶体,采用铟焊工艺将其焊接到水冷系统上,用可调式恒温水箱对其进行温度控制。
2)  Yb:YAG
Yb:YAG晶体
1.
Infrared Scintillation Properties of Yb∶YAG Crystal;
Yb∶YAG晶体的红外闪烁特性
2.
Growth of Yb∶YAG Crystal and Its Laser Performance;
Yb∶YAG晶体的生长与激光性能
3)  Yb:YAG crystal
Yb:YAG 晶体
4)  (Cr,Yb):YAG crystal
（Cr,Yb）YAG晶体
5)  (Cr,Yb):YAG crystal
（Cr,Yb）:YAG晶体
6)  Yb
Yb
1.
MICROSTRUCTURES AND MECHANICAL PROPERTIES OF AS-CAST Mg-xYb AND Mg-xYb-0.4Zr ALLOYS;
Mg-xYb和Mg-xYb-0.4Zr合金的铸态组织及力学性能
2.
Study on Growth and Cracking of Cr,Yb,Ho:YAGG Tunable Laser Crystal;
Cr,Yb,Ho:YAGG可调谐激光晶体生长及开裂研究
3.
Synthesis of High Luminescent Y_2O_3∶Er,Yb Upconversion Nanocrystals;
高发光强度上转换材料Y_2O_3∶Er,Yb纳米晶的制备