1) mechanism of the catalytic aquathermolysis
水热裂解催化机理
2) hydrothermal cracking catalyst
水热裂解催化剂
4) catalytic aquathermolysis
催化水热裂解
1.
For the UHCO having undergone the catalytic aquathermolysis under the optimal reaction conditions,the viscosity at 50℃ was decreased from 524.
2%,pH值12;在优化条件下经催化水热裂解的实验超稠油,50℃黏度由524。
5) catalytic thermal cracking
催化热裂解
1.
This paper concerns the small-scale test and industrial amplification test in activity components of catalytic thermal cracking catalyst respectively, as well as the initial research in reaction mechanism.
催化热裂解技术是以减压馏分油和渣油为原料,使用以ZSM-5分子筛为主要活性组元的固体酸催化剂,在催化裂化装置上,在一定的工艺条件下生产乙烯和丙烯为主的低碳烯烃的一项新工艺。
6) Catalytic pyrolysis process
催化热裂解
1.
CEP-1 catalyst is a new type proprietary catalyst for catalytic pyrolysis process (CPP), its main active component is phosphorus and alkali earth metal contained medified pentasil structure zeolite.
CEP-1催化剂是一种新型的催化热裂解工艺专用催化剂,其活性组分为含磷及碱土金属的改性五元环族沸石。
补充资料：中压压热釜非催化油脂水解法
分子式：
CAS号：
性质：一种使用很广的油脂水解工艺方法。当油脂与水的反应温度达到225℃，就可以无需催化剂进行水解而达到较高的反应速率，并实现连续化。操作压力要高于反应温度下的饱和压力(不低于3MPa)，以保持反应系统处于液相状态。反应过程是逆流的，并分为3段进行。每段都经过静置分层以降低油相中的甘油含量，有利于提高水解率，最终可达到97％。已实现工业化的方法有多种。使用较多的有Gianazza法和Construzioni Meccaniche Bernardini法。
CAS号：
性质：一种使用很广的油脂水解工艺方法。当油脂与水的反应温度达到225℃，就可以无需催化剂进行水解而达到较高的反应速率，并实现连续化。操作压力要高于反应温度下的饱和压力(不低于3MPa)，以保持反应系统处于液相状态。反应过程是逆流的，并分为3段进行。每段都经过静置分层以降低油相中的甘油含量，有利于提高水解率，最终可达到97％。已实现工业化的方法有多种。使用较多的有Gianazza法和Construzioni Meccaniche Bernardini法。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。