1) H_2S partial pressure
H_2S分压
1.
Effects of high H_2S partial pressure on corrosion behavior of API-X60 pipeline steel were discussed.
利用高温高压反应釜模拟高含硫气田H_2S/CO_2共存环境,分别在流动湿气和溶液介质中进行API-X60腐蚀实验,探讨了高H_2S分压对腐蚀行为的影响。
3) H2S
H_2S
1.
The analysis of the causes of hydrogen blistering, development process and corrosion of the spherical tanks in wet H2S environment concludes that hydrogen blistering is the results of hydrogen permeation into steel in hydrogen environment of the tank and the existence of impurities and cavities in steel material.
对湿H_2S环境下球罐氢鼓泡的产生原因、形成过程和腐蚀状况进行了分析,指出氢鼓泡的发生一是球罐处于临氢环境,因腐蚀产生的[H]渗入到了钢中;二是容器所用的钢材存在夹杂,即有“空穴”。
2.
The absorbent could remove H2S and HC1 from automotive LPG so that it passed the copper strip corrosion test, thus achieving good economic and social benefit.
针对扬子石化股份公司芳烃厂液化气装置生产的车用液化气钢片腐蚀不合格的问题,采用NC-L型双功能吸附剂,有效地脱除车用液化气中的H_2S和HCl,使其铜片腐蚀指标合格,取得了良好的经济和社会效益。
3.
The inhibitive effect of each sulfourea and cetylpyridinium bromide and their synergistic inhibitive effect on 16Mn steel under thin electrolyte film with H2S were investigated by using potentiodynamic polarization technique and EIS.
用极化曲线和交流阻抗技术研究了硫脲和溴化十六烷基吡啶在复配前后对含H_2S薄层液膜下的16Mn钢的缓蚀行为,得到了一些重要结论,并对其进行解释和讨论。
5) grouping of H_2's system
H_2S 系统分组
6) H_2S/SO_2 in-line analyzer
H_2S/SO_2在线分析仪
补充资料：道耳顿分压定律
关于混合气体压强的实验定律，是J.道耳顿于1802年发现的。这一定律可以表述为：容器中混合气体对器壁所产生的压强等于在同样温度、体积条件下组成混合气体各成分单独存在时的分压强之和。
道耳顿分压定律只适用于混合的理想气体，对于实际气体，此定律只在压强较低时才近似地成立。若各种气体的分子数密度分别为n1,n2,...，则这些气体施于器壁的分压强分别为p1=n1kT，p2=n2kT,...，所以总压强为。
这就是道耳顿分压定律的数学表示。
在实际问题中，常用质谱分析法测量各分压强。
道耳顿分压定律只适用于混合的理想气体，对于实际气体，此定律只在压强较低时才近似地成立。若各种气体的分子数密度分别为n1,n2,...，则这些气体施于器壁的分压强分别为p1=n1kT，p2=n2kT,...，所以总压强为。
这就是道耳顿分压定律的数学表示。
在实际问题中，常用质谱分析法测量各分压强。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条