The analysis of the causes of hydrogen blistering, development process and corrosion of the spherical tanks in wet H2S environment concludes that hydrogen blistering is the results of hydrogen permeation into steel in hydrogen environment of the tank and the existence of impurities and cavities in steel material.
对湿H_2S环境下球罐氢鼓泡的产生原因、形成过程和腐蚀状况进行了分析,指出氢鼓泡的发生一是球罐处于临氢环境,因腐蚀产生的[H]渗入到了钢中;二是容器所用的钢材存在夹杂,即有“空穴”。
2.
The absorbent could remove H2S and HC1 from automotive LPG so that it passed the copper strip corrosion test, thus achieving good economic and social benefit.
针对扬子石化股份公司芳烃厂液化气装置生产的车用液化气钢片腐蚀不合格的问题,采用NC-L型双功能吸附剂,有效地脱除车用液化气中的H_2S和HCl,使其铜片腐蚀指标合格,取得了良好的经济和社会效益。
3.
The inhibitive effect of each sulfourea and cetylpyridinium bromide and their synergistic inhibitive effect on 16Mn steel under thin electrolyte film with H2S were investigated by using potentiodynamic polarization technique and EIS.
用极化曲线和交流阻抗技术研究了硫脲和溴化十六烷基吡啶在复配前后对含H_2S薄层液膜下的16Mn钢的缓蚀行为,得到了一些重要结论,并对其进行解释和讨论。
6) sodium chloride
NaCl
1.
Effect of sodium chloride and sodium sulfate on the seed germination and seedlings establishment of Chinese dandelion;
NaCl和Na_2SO_4胁迫对蒲公英种子发芽及成苗的影响
2.
The influence of three different salts on the forming of granular resistant starch was studied and the results showed that the optimum amount of sodium chloride and potassium chloride content was 20% and 12% respectively.
文中考察了盐(NaCl、KCl和CaCl2)对颗粒态抗性淀粉形成的影响,得出NaCl和KCl的最适添加量分别为20%和12%,而CaCl2的添加对抗性淀粉形成不利。
3.
High-amylose cornstarch was used as material to study on effects of concentrations of sodium chloride and glucose on the formation of RS.
以高直链玉米淀粉为试材,分别研究了NaCl浓度和葡萄糖浓度对抗性淀粉形成的影响,发现当NaCl浓度提高到10%以上时,抗性淀粉得率从10。
补充资料：包裹体
见包裹体地球化学、地质温度计。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条