1) oxidation wear
氧化磨损
1.
The rules of diffusion and oxidation wear for PCBN tool were studied based on thermodynamics.
从热力学的角度研究了PCBN刀具扩散磨损和氧化磨损规律,利用热力学模型计算不同温度下PCBN刀具加工钢铁、镍基合金、铝合金和钛合金时刀具材料扩散溶入工件材料中的浓度值。
2.
Adhesive wear,oxidation wear and diffusion wear were the main wear mechanisms of the cemented carbide tool.
研究结果表明,使用硬质合金刀具材料高速干车削Ti-6Al-4V时,刀具的磨损机理主要为粘结磨损、氧化磨损和扩散磨损。
3.
Diffusion and oxidation wear are the main wear mechanisms at such high temperature.
高速切削金属件的时候,切削温度高达800—1000℃以上,扩散氧化磨损成为PCD刀具的主要磨损原因。
2) Oxidation-delamination wear
氧化剥层磨损
3) oxidation wear and delamination damage
氧化磨损和脱层损伤
4) chemical wear
化学磨损
5) wear and hardening
磨损和硬化
1.
The inspection and analysis showed that the fracture of wire rope was fatigue fracture,which was due to the severe friction and bend fatigue existing in the rope running process with load,resulted in the wear and hardening of the wire surface and some spalling pits and cracks presented at the wear surface o.
检验分析表明 ,钢丝绳的断裂属性为疲劳断裂 ,疲劳断裂原因是由于钢丝绳在运行过程中受到严重摩擦和弯曲振动载荷 ,使其表面磨损和硬化 ,并在磨损面出现剥落坑和小裂纹 ,成为疲劳源 ,最终导致疲劳断
6) fluidized attrition
催化剂磨损
补充资料：二羟基氧化丙烯-氧化乙烯共聚醚
分子式：
分子量：
CAS号：
性质：一种破乳剂。蜡状粘稠液体。羟值≤50毫克KOH/毫。应用于原油脱水，配成一定浓度的水溶液即可使用。经氢氧化钾为催化剂，丙二醇与环氧丙烷、环氧乙烷 开环聚合而成。
分子量：
CAS号：
性质：一种破乳剂。蜡状粘稠液体。羟值≤50毫克KOH/毫。应用于原油脱水，配成一定浓度的水溶液即可使用。经氢氧化钾为催化剂，丙二醇与环氧丙烷、环氧乙烷 开环聚合而成。