1) CO/ECO blend
CO/ECO共混胶
2) ECO reclaim
ECO再生胶
1.
The results showed that producing ECO reclaim by mechanical process was feasible, the optimal reclaiming conditions was nip 0.
研究了机械法再生硫化共聚氯醚橡胶(ECC))薄通次数及辊距对其性能的影响以及ECO再生胶的硫化体系的配合,结果表明通过适当机械再生工艺制造的ECO再生胶是可行的。
3) PET/PET-CO-PEN blend
PET/PET-co-PEN共混物
1.
The blow molding processing characteristics of PET/PET-CO-PEN blend is introduced.
介绍聚对苯二甲酸乙二酯(PET)/PET共聚聚萘二甲酸乙二酯(PET-co-PEN)共混物的成型加工特性,探讨利用加工PET的设备、两步法注射拉伸吹塑工艺,生产耐热和阻隔PET/PET-co-PEN共混物制品的可行性。
4) blend
[英][blend] [美][blɛnd]
共混胶
1.
Study on Irradiation Modification of Plasticzied PVC/NBR Blend;
增塑PVC/NBR共混胶的辐照改性
2.
The physical-mechanical properties and viscoelastic properties of 20 phr 3,4-IR blends of SBR or NR were studied.
6℃]与SBR或NR质量比为20/80组成的共混胶的力学性能和粘弹性能。
3.
The formula,technology and main properties of EVA/NBR/NR blend in making oil resistant microcellular sole have been introduced.
介绍ＥＶＡ／ＮＢＲ／ＮＲ三元共混胶在耐油环境中使用的微孔鞋底的配方、工艺及主要性能。
5) blend latex
共混胶乳
1.
It was found that the mixing process and stability of blend latex were strongly affected by polymeric polarity and amount of emulsifer in original latex under the present experiment conditions.
对乳液最低成膜温度（ＭＦＴ）、胶膜硬度及耐水性的研究表明：质量比为１１的ＰＢＡ／ＰＭＭＡ共混胶膜和Ｐ（ＢＡ－ＭＭＡ）共聚胶膜的连续相组成相近；而对于同样组成的ＰＢＡ／ＰＳｔ共混胶膜，分散在连续相中的ＰＳｔ所占比例明显高于Ｐ（ＢＡ－Ｓｔ）共聚胶膜；ＰＢＡ／ＰＳｔ共混胶乳的使用性能不仅取决于其组成，还取决于成膜温度和使用温
6) hybrid micelle
共混胶束
补充资料：共混胶形态特征
分子式：
CAS号：
性质：指不同橡胶或橡胶与塑料经机械混炼后的结构形态。从各成分的混合形态来看，多为不均的“相”混合。如在共混胶中占份量多的成分，在胶相结构上形成连续相，将份量少的成分包围起来。即形成海与岛的形态。如果共混的各成分切割成互不连续的小微区，则称为交错的岛与岛的形态。混炼好的共混胶相结构尺度可达1～2μm。共混各组分的黏度对共混胶形态(即相结构)影响最大，黏度低的橡胶易形成连续相。另外，填加炭黑等填充剂，胶相结构尺度会变得细小。所以共混胶的形态特征是典型的微观多相体系。
CAS号：
性质：指不同橡胶或橡胶与塑料经机械混炼后的结构形态。从各成分的混合形态来看，多为不均的“相”混合。如在共混胶中占份量多的成分，在胶相结构上形成连续相，将份量少的成分包围起来。即形成海与岛的形态。如果共混的各成分切割成互不连续的小微区，则称为交错的岛与岛的形态。混炼好的共混胶相结构尺度可达1～2μm。共混各组分的黏度对共混胶形态(即相结构)影响最大，黏度低的橡胶易形成连续相。另外，填加炭黑等填充剂，胶相结构尺度会变得细小。所以共混胶的形态特征是典型的微观多相体系。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条