1) Ni-based composite coating
镍基复合刷镀层
2) Ni matrix composite coatings with Al2O3
镍基Al2O3复合镀层
3) nickel composite coating
镍基复合镀层
1.
In this thesis, the pretreatment for nickel composite coatings were investigated aimed at good adhesion.
本文以探索良好结合力的镀层为目的,对镍基复合镀层工件的前处理工艺进行了研究,通过电化学工作站等仪器对镀层的性能进行了分析。
4) composite nickel coating
复合镀镍层
1.
Compared with the rusting time on 5% NaCl solution,the time of composite nickel coating containing rust preventive oil microcapsules is 40 times that of the nickel coating without microcapsul.
通过比较,含有防锈润滑油微胶囊的复合镀镍层在5%NaCl溶液中出现腐蚀锈点的时间是普通镀镍层的40倍以上;含苯并三氮唑缓蚀剂的微胶囊复合镀铜层耐氨水点滴及硝酸点滴腐蚀时间是普通镀铜层的3倍左右;含憎水剂微胶囊的复合镀铜层在硫酸溶液中的电极电位随时间变化规律和阳极极化曲线表明,其比普通镀铜层具有更好的耐腐蚀性。
5) Ni based composite coating
镍复合镀层
6) composite coating
复合刷镀层
1.
A pure nickel coating and n-Al2O3/Ni composite coating were prepared.
制备了纯镍刷镀层和镍基纳米氧化铝复合刷镀层。
2.
To research the wear mechanics of nano-particle composite coating in lubricated condition with sand in oil,a nickel matrix nano-Al_2O_3 composite coating was prepared.
为研究纳米颗粒复合电刷镀层在含沙粒油润滑条件下的磨损机制,首先制备了镍基纳米A l2O3复合电刷镀层,采用T-11球盘式磨损试验机进行复合刷镀层在含沙粒油润滑条件下的磨损试验,采用FTP-X2型分析式铁谱仪对复合镀层磨损试验后的润滑油中的磨粒形貌进行了研究。
补充资料:镍-镉扩散镀层
分子式:
分子量:
CAS号:
性质:就是先在零件上镀一层镍(12-15微米),然后在镍层上再镀一层镉(3-5微米),最后在335℃下进行1小时的扩散处理。形成镍镉金属间化合物的扩散层,熔点高,在500℃下具有良好的热稳定性,并具有良好的抗氧化性、耐热和耐蚀性。对基底材料抗应力腐蚀性能有很大提高,它适用于中温高强度钢、低合金钢和不锈钢的防护。对工作温度低于500℃的零件能提供良好的防护性能。过去这些零件采用镀镉防护,但隔层的使用温度只能在230℃以下,否则就不能起防护作用,并会引起一些材料的镉脆。改用镍镉扩散镀层,能满足防护要求。镍镉扩散镀层已应用于航空工业。
分子量:
CAS号:
性质:就是先在零件上镀一层镍(12-15微米),然后在镍层上再镀一层镉(3-5微米),最后在335℃下进行1小时的扩散处理。形成镍镉金属间化合物的扩散层,熔点高,在500℃下具有良好的热稳定性,并具有良好的抗氧化性、耐热和耐蚀性。对基底材料抗应力腐蚀性能有很大提高,它适用于中温高强度钢、低合金钢和不锈钢的防护。对工作温度低于500℃的零件能提供良好的防护性能。过去这些零件采用镀镉防护,但隔层的使用温度只能在230℃以下,否则就不能起防护作用,并会引起一些材料的镉脆。改用镍镉扩散镀层,能满足防护要求。镍镉扩散镀层已应用于航空工业。