Protecting technique and protecting effect of electroless Ni-W-P alloy plating on 65Mn steel in heat treatment process were studied.
介绍了化学镀Ni-W-P合金对65Mn钢热处理的表面防护工艺及效果。
2.
In order to study the effects of pulse parameters on deposit rate, contents of W and P in coatings, corrosion resistance and hardness, pulse electrodepositing Ni-W-P alloy technology was studied by weighing, immersing in H_2SO_4 solution, EPMA-1600 electron probe and HX-1 microhardness tester.
为了研究Ni-W-P合金脉冲电沉积中脉冲参数对镀速和镀层中钨、磷含量的影响以及对镀层耐蚀性和硬度的影响,采用称重法、硫酸浸泡法、日本岛津EPMA-1600型电子探针以及HX-1型显微硬度计对Ni-W-P合金工艺进行了研究。
3.
The electrodeposition characteristics,structure and microhardness of Ni-W-P alloy have been studied by the methods of cyclic voltammetry, potentiostatic step and X-ray diffraction(XRD).
应用循环伏安、恒电位阶跃和 X射线衍射（ XRD）等方法研究了 Ni-W-P合金电沉积特点和镀层结构与显微硬度 。
5) W-Mo-Ni-Fe alloy
W-Mo-Ni-Fe合金
1.
A method determining W, Mo, Ni and Fe contents at the same time for W-Mo-Ni-Fe alloy by using energy diffuse X-ray fluorescence (EDXRF) spectroscopy is described.
介绍了用能量色散X射线荧光光谱法(EDXRF)同时测定W-Mo-Ni-Fe合金组分的分析方法。
6) Ni-Cr-W-Mo alloy
Ni-Cr-W-Mo合金
补充资料：Ni3Al基金属间化合物高温合金
Ni3Al基金属间化合物高温合金
Ni_(3)Al-base intermetallic compound superalloy
N一3AIJ一J旧shuJ一an huahewu goowen heJ一nNi3AI基金属间化合物高温合金(Ni3AI一baseintermetallie eompound superalloy)以Ni3AI相为基体的金属间化合物高温合金。Ni3AI作为高温合金材料中的强化相口)早已被人们所熟知。单晶Ni3AI有较好的室温塑性和加工性，但多晶Ni3AI在室温的塑性儿乎为零。1979年，日本和泉修等发现，添加微量硼可使Ni3AI韧化。硼强烈地偏聚于晶界，从而提高晶界的结合强度并使晶界区无序化，因此提高了晶界区塑性变形能力，使Ni3AI的室温拉伸伸长率可达50%以上。纯净N珠AI的室温、高温强度偏低，与高温合金相比需要进一步提高。固溶强化(见高温合金固溶强化)是提高强度的一条有效途径。Ni3AI可以固溶很多元素，其中以错和铅的强化效果最显著。美国橡树岭国家试验室已发展了一系列含铬、错、错等元素的Ni3AI基金属间化合物高温合金，具有良好的强度、塑性和高温抗氧化性。中国也对Ni3AI基合金进行了深入研究，并添加微量镁显著改善了热加工塑性。Ni3AI基合金可能是最先在工业上得到使用的金属间化合物高温合金之一，已制成各种部件在试用，如汽轮机和柴油机的耐热部件、高温模具、加热元件以及航空用的紧固件等。 〔邹敦叙)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条