1)  (poly)VAc
（聚）醋酸乙烯
2)  PVAc
聚醋酸乙烯
1.
Synthesis of Low Polymerization Degree PVAc and the Rheologic Features of Reaction Liquid;
低聚合度聚醋酸乙烯合成与反应液流变特性
2.
Study on Preparation of Wall Brick from the BF Slags Containing Titania and the PVAC;
聚醋酸乙烯乳液制高炉渣墙体砖的研究
3.
In this experiment, by adding molecular adjustor and optimizing the experimental condition through orthogonal test, low molecular weight PVAc was firstly synthesized and then with NaOH as.
采用溶液聚合法,以醋酸乙烯为单体,偶氮二异丁腈为引发剂,甲醇为溶剂,加入分子量调节剂,通过多次实验优化实验条件,合成低相对分子质量的聚醋酸乙烯(PVAc),后者以NaOH为催化剂,经醇解得到了外观为白色粉末状、平均聚合度为600,醇解度为80%的低相对分子质量的PVA产品。
3)  polyvinyl acetate
聚醋酸乙烯
1.
Study on the modified enviromental protection of polyvinyl acetate(PVAc) emulsion;
环保型聚醋酸乙烯酯乳液的改性研究
2.
Study on polyvinyl acetate emulsion modified by silicone;
有机硅改性聚醋酸乙烯乳液胶粘剂的研究
3.
A complete mathematical model based on the reaction mechanism for the production of polyvinyl acetate was developed.
利用现场工况数据 ,模型可以实时预报醋酸乙烯的转化率、各组分物料浓度、聚醋酸乙烯聚合度等重要参数。
4)  poly(vinyl acetate)
聚醋酸乙烯
1.
Using N,N,N′,N′-tetramethylethylenediamine and potassium persulphate as a redox initiation system,high molecular weight poly(vinyl acetate)(PVAc) was synthesized by aqueous deposited polymerization.
以N,N,N,′N′-四甲基乙二胺-过硫酸钾为氧化-还原引发体系,用水相沉淀聚合法合成了超高相对分子质量的聚醋酸乙烯(PVAc)。
5)  Polyvinylacetate
聚醋酸乙烯酯
1.
Polyvinylacetate (PVAc) and a random copolymer of poly(vinyl acetate-co-isopropenyl acetate) (PVIPA) with number-average molecular weight (M_n) around 2×104?g/mol and molecular weight distribution(MWD,M_w/M_n<2.
5)的聚醋酸乙烯酯(PVAc)和醋酸乙烯酯(VAc)与醋酸异丙烯酯(IPAc)的无规共聚物聚(PVIPA)。
6)  poly(vinyl acetate)
聚醋酸乙烯酯
1.
Effects of initiation systems[ammonium persulfate-sodium hydrogen carbonate(I1),azodiisobutyronitrile(I2) and peroxide-ascorbic acid(I3)] on microemulsion polymerization of poly(vinyl acetate) were investigated.
考察了3种引发体系[过硫酸铵-碳酸氢钠(I1),偶氮二异丁腈(I2),过氧化氢-抗坏血酸(I3)]对聚醋酸乙烯酯微乳液聚合的影响。
2.
Iodic-end-group poly(vinyl acetate)(PVAc-I) was synthesized from vinyl acetate(VAc) by degenerative chain transfer radical polymerization in presence of iodine with 2.
以偶氮二异丁腈为引发剂,在醋酸乙烯酯(VAc)的普通自由基聚合反应体系中加入少量碘,原位生成了碘化物α-碘代异丁腈,该碘化物在聚合过程中起可逆的链转移剂的作用,合成了含碘端基的聚醋酸乙烯酯(PVAc-I);考察了反应温度、原料配比对聚合反应的影响。
3.
Through telomerization of vinyl acetate by tetrachloride carbon,poly(vinyl acetate) with chlorine atom in the end of macromolecules(PVAc-CCl_3) was synthesized;2.
通过CCl4调聚反应制备出了末端带有氯原子的聚醋酸乙烯酯(PVAc),进一步引发苯乙烯原子转移自由基聚合得到聚醋酸乙烯酯-b-聚苯乙烯嵌段共聚物(PVAc-b-PSt),此嵌段共聚物与偶联剂二乙烯基苯反应后醇解,得到了聚乙烯醇-b-聚苯乙烯星形嵌段共聚物(PVA-b-PSt)n。
参考词条
补充资料：聚醋酸乙烯


聚醋酸乙烯
Polyvinyl Acetate

　　ju聚醋敌乙烯第8卷 (6)其它助剂醋酸乙烯乳液聚合时，常用缓冲剂.其目的有二:一是稳定引发剂的分解速率，引发剂的分解速率受pH值影响，而引发剂的分解又会导致聚合体系pH值的变化;二是醋酸乙烯的水解速率对pH值很教感，在反应过程中应使单体水解速率降到最小。一般醋酸乙烯系乳液的pH值为4~6，也有特殊低于或高于这个范围的。 2.2.4.2.生产方法 (l)间歇法乳液聚合法生产乳液的装置如图3所示.首先将加有乳化剂(或保护胶体)的水溶液加入带夹套的聚合反应器中，一边加热，一边搅拌，当达到反应温度时，连续滴加单体和引发剂进行聚合，当反应率几乎达百分之百时，将聚合反应器内物料冷却到规定温度，出料，包装为成品。合的工艺流程。环形反应器是由不锈钢环形长盘管构成，可以有几个进出口，环形反应器的两端分别和循环泵的进出口相连。由计量泵将原料连续加入反应器，由循环泵将环形反应器中物料循环，使反应器中总是充满物料，生成物以和投料量相等的速度出料。反应器出口管上有一压力控制阀，其作用是保持反应器中适当的压力。VAC┌──┐ │!业 │ └──┘ ┌─┬─┐ │2_│ │ └─┴─┘ ┌──┐ │生’│ └──┘┌─┐ │1l│ └─┘ ┌──┐ │/尸 │ ┌───┐ │、 │ │口~、 │ │l尸 │ │ │ └──┘ │ │ └───┘ ┌─┐ │4 │ └─┘ 凝器 图礴连续式乳液聚合工艺流程图 1一单体槽;2一水相槽;3一计量泵;4一循环泵;5一环形反应器;6一后添加剂槽;7一混合槽，8一过溥网2·么5. vAE共聚乳液 图3乳液聚合过程装置l一溶解釜;2一聚合釜;3一成品槽 醋酸乙烯一乙烯共聚乳液是在一定压力下聚合而成的。其工艺流程如图5所示，反应系统由聚合反应釜、循环泵、换热器、外撤热循环系统等组成。