1.
Synthesis of Low Polymerization Degree PVAc and the Rheologic Features of Reaction Liquid;
低聚合度聚醋酸乙烯合成与反应液流变特性
2.
Study on Preparation of Wall Brick from the BF Slags Containing Titania and the PVAC;
聚醋酸乙烯乳液制高炉渣墙体砖的研究
3.
In this experiment, by adding molecular adjustor and optimizing the experimental condition through orthogonal test, low molecular weight PVAc was firstly synthesized and then with NaOH as.
采用溶液聚合法,以醋酸乙烯为单体,偶氮二异丁腈为引发剂,甲醇为溶剂,加入分子量调节剂,通过多次实验优化实验条件,合成低相对分子质量的聚醋酸乙烯(PVAc),后者以NaOH为催化剂,经醇解得到了外观为白色粉末状、平均聚合度为600,醇解度为80%的低相对分子质量的PVA产品。
5) polyvinyl acetate
聚醋酸乙烯
1.
Study on the modified enviromental protection of polyvinyl acetate(PVAc) emulsion;
环保型聚醋酸乙烯酯乳液的改性研究
2.
Study on polyvinyl acetate emulsion modified by silicone;
有机硅改性聚醋酸乙烯乳液胶粘剂的研究
3.
Preparation of polyvinyl acetate/montmorillonite composite latex and it's property
聚醋酸乙烯/蒙脱土复合乳液的制备及性能
6) poly(vinyl acetate)
聚醋酸乙烯
1.
Using N,N,N′,N′-tetramethylethylenediamine and potassium persulphate as a redox initiation system,high molecular weight poly(vinyl acetate)(PVAc) was synthesized by aqueous deposited polymerization.
以N,N,N,′N′-四甲基乙二胺-过硫酸钾为氧化-还原引发体系,用水相沉淀聚合法合成了超高相对分子质量的聚醋酸乙烯(PVAc)。
补充资料：聚氯乙烯/乙烯-醋酸乙烯共聚物共混物
分子式：
CAS号：
性质：系聚氯乙烯与乙烯-醋酸乙烯共聚物或氯乙烯接枝乙烯-醋酸乙烯共聚物组成的共混物。醋酸乙烯含量30％～45％左右的EVA共聚物可作为聚氯乙烯的冲击改性剂，加入5～8份可使简支梁缺口冲击强度达20kJ/m2以上，且耐候性好。用于门窗型材等户外使用的塑料建材方面，高醋酸乙烯含量的共聚物可作为增塑聚氯乙烯的永久型增塑剂，用于软制品方面。
CAS号：
性质：系聚氯乙烯与乙烯-醋酸乙烯共聚物或氯乙烯接枝乙烯-醋酸乙烯共聚物组成的共混物。醋酸乙烯含量30％～45％左右的EVA共聚物可作为聚氯乙烯的冲击改性剂，加入5～8份可使简支梁缺口冲击强度达20kJ/m2以上，且耐候性好。用于门窗型材等户外使用的塑料建材方面，高醋酸乙烯含量的共聚物可作为增塑聚氯乙烯的永久型增塑剂，用于软制品方面。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条