1) slag
[英][slæɡ] [美][slæg]
炼渣
1.
The results from physical test show that the melting temperature of the slag from Lidegui site is higher than 1280℃.
物理测试结果表明,遗址炼渣的熔融温度高于1280℃;成分分析结果表明,李德贵炼渣中铜含量很低,远低于炼铜渣的铜含量;而其铁含量很高,与欧洲早期铁器时代和罗马时代的块炼铁渣相近;物相分析结果表明,李德贵炼渣的主要物相与炼铜渣没有区别,但炼铜渣中发现一些铜氧化矿和硫化矿。
2.
All samples of copper ores, slag and copper ingots are from the ancient sites of mining and smelting, which include Tonglüshan site in Hubei province, Zhaobishan site in Ningxia municipality, Zhongtiaoshan site in Shanxi province and Dajing site in Inner Mongolia municipality autonomous region.
实验采用电感藕合等离子体发射光谱仪(ICP-AES)测试了湖北铜绿山、宁夏照壁山、山西中条山和内蒙古林西大井古代矿冶遗址的铜矿石,炼渣和铜锭的稀土元素含量,通过对其稀土总量和稀土配分模式的对比研究,探讨了稀土元素在古代铜矿冶炼过程中的化学行为。
2) refining slag
精炼渣
1.
Effect of foaming agent on foaming performance of LF refining slag with high basicity;
发泡剂对高碱度LF精炼渣泡沫化性能的影响
2.
Development of LF refining slag and research on the cleanness of ML08Al CC billets;
ML08Al钢精炼渣开发及铸坯洁净度研究
3) refining slag
精炼渣系
1.
Factors related to increase ot Al content such as refining slag compositions,molten steel composition LF refining time etc.
通过理论计算和工业生产实践研究了不同的渣系、钢水成分、处理时间等对LF精炼过程增铝的影响,不同精炼渣系下钢中夹杂的组成,结果表明采用CaO-SiO2渣系LF处理过程几乎不发生增铝现象,而采用CaO-Al2O3渣系随着处理时间的延长以及钢种成分的区别,钢中铝有不同程度的增加,生产实践结果与理论计算趋势基本一致。
2.
The desulfurization effect for both CaO-Al2O3-MgO-SiO2 and CaO-Al2O3-MgO-SiO2-CaF2 refining slag are studied in ladle furnace process.
在钢包精炼炉上对CaO-Al2O3-MgO-SiO2和CaO-Al2O3-MgO-SiO2-CaF2两种精炼渣系的脱硫效果进行了研究。
4) refining furnace slag
冶炼炉渣
1.
The present status of the research of glass-ceramics by industrious solid waste as materials such as industrial slag, tailings, and refining furnace slag was s ummarized.
概述了以工业废渣、尾矿尾砂、冶炼炉渣等工业固体废弃物为原料制备微晶玻璃的研究现状。
5) lead slag
炼铅炉渣
1.
There Was a kind of lead slag in Yunnan which contains zinc and indium,but subjected to the metallurgy technology,they were unable to be recovered but stocked before.
云南某铅冶炼厂鼓风炉炼铅炉渣富集有价金属锌、铟等,以前受冶炼技术条件限制而无法回收,只能长期堆存。
2.
Lead slags sometimes contain metal high and the fitted conditions were not eligible, so some plants take order with lead slag lately and make largeness abandon.
云南省大部分的铅生产都采用鼓风炉法，炼铅炉渣中一般含有铅、锌、铟等有价金属，以前由于冶炼技术条件的制约，炉渣中的有价金属没有得到回收利用。
3.
Therefore,the recovery and utilization of lead slag can save precious resources,increase the comprehensive utilization ratio of raw material,raise economic benefit and reduce environmental pollution.
鼓风炉炼铅炉渣中由于含有锌、铅等有价金属,具有极高的回收价值。
6) top-slag refining
顶渣精炼
1.
Therefore,choosing top-slag refining process for the converters less than 40t can effectively improvemol the steel quality and have low runningcost.
介绍了利用CAS-OB装置在惰性气体保护下进行顶渣精炼工艺过程。