1) bitumen vein
炭沥青脉
2) pitch derived carbon
沥青炭
1.
Bulk density,porosity of pitch derived carbon were determined.
将高温煤沥青和浸渍剂沥青在不同压力下炭化,在2500℃下对所得沥青炭进行石墨化处理;测试了所得沥青炭的体积密度、开孔率;利用扫描电子显微镜(SEM)观察了所得沥青炭的显微结构;利用XRD检测了所得沥青炭石墨化处理后的石墨化度;测试了所得沥青炭的压缩强度。
2.
Pitch derived carbons were prepared from high temperature pitch and impregnating pitch by carbonization at different pressures and graphitization at 2 500℃.
将高温煤沥青和浸渍剂沥青在不同压力下炭化,在2 500℃下对所得沥青炭进行石墨化处理。
3.
Scanning electron microscopy(SEM) was used to observe the morphology of pitch derived carbons.
将高温煤沥青和浸渍剂沥青在92M Pa下炭化,在2 500℃下对所得沥青炭进行石墨化处理;测试了所得沥青炭的体积密度、开孔率、比表面积(SBET);利用扫描电子显微镜(SEM)观察了所得沥青炭的显微结构;利用X射线衍射方法(XRD)检测了所得沥青炭石墨化处理后的石墨化度;测试了所得沥青炭的氧化性能;测试了沥青炭试样的比热容、导热系数、热扩散率和线膨胀系数。
3) coal-tar pitch derived carbon
煤沥青炭
1.
Contrast studies on microstructure and properties of three kinds of coal-tar pitch derived carbon;
3种煤沥青炭微观结构及其性能的对比研究
4) pitch coke
沥青焦炭
5) pitch peat
沥青泥炭
6) Medium temperature pitch-derived carbon
中温沥青炭
补充资料：沥青基活性炭纤维
分子式：
CAS号：
性质：由各向同性沥青原丝制成的活性炭纤维。比表面积700～2500m2/g，平均微孔直径1.7～2.6nm，微孔容积0.3～1.6ml/g，甲苯吸附性22％～122％，碘吸附性850～2200mg/R，甲基蓝吸附性130～400ml/g，着火温度480℃。制法是将通用级沥青纤维稳定化、碳化与活化而得。用途是溶剂回收、有害气体吸附材料、合成氨纯化滤材、纯水制造、催化剂载体、人工脏器及电极材料等。
CAS号：
性质：由各向同性沥青原丝制成的活性炭纤维。比表面积700～2500m2/g，平均微孔直径1.7～2.6nm，微孔容积0.3～1.6ml/g，甲苯吸附性22％～122％，碘吸附性850～2200mg/R，甲基蓝吸附性130～400ml/g，着火温度480℃。制法是将通用级沥青纤维稳定化、碳化与活化而得。用途是溶剂回收、有害气体吸附材料、合成氨纯化滤材、纯水制造、催化剂载体、人工脏器及电极材料等。