2) Surface-coated modification
表面涂覆改性
3) coating
[英]['kəʊtɪŋ] [美]['kotɪŋ]
表面包覆
1.
Through the thermodynamic anal ysis of coating process,it was proved that Al(OH)3 nucleus coating Ti(OH)4 c ompetes with Al(OH)3 film coating Ti(OH)4.
热力学分析表明,在纳米Ti(OH)4表面包覆Al(OH)3的过程中,存在核包覆和膜包覆的竞争;而在其它条件不变的情况下,包覆物的过饱和度对包覆形态起到了决定性的影响。
2.
Through the thermodynamic analysis of coating process, it was proved that Al_2O_3 nucleus coating TiO_2 competes with Al_2O_3 film coating TiO_2.
热力学分析表明,用化学液相沉积法在纳米TiO2表面包覆氧化铝的过程中,存在核包覆和膜包覆的竞争;而在其它条件不变的情况下,包覆物的过饱和度对包覆形态起到了决定性的影响。
3.
Studies were focused on the effects of different amounts of cobalt coating on structure and electrochemical characteristics of Ni(OH)_2.
通过“管道式合成”工艺制备了球形氢氧化镍,然后以化学沉积法在氢氧化镍表面包覆氢氧化钴,制备了表面覆钴含量不同(0。
4) surface coating
表面包覆
1.
Research on surface coating of nanoscale titania;
纳米二氧化钛表面包覆的研究
2.
Effect of surface coating by ball milling on cycle stability of Mg-based hydrogen storage electrodes;
球磨表面包覆对镁基贮氢合金电化学性能的影响
5) Surface modification
表面包覆
1.
Surface modification of CaSiO3∶Pb, Mn phosphors was carried out by coating transparent conductive films of Al-doped zinc oxide which were formed by homogeneous phase co-precipitation and heat treatment process.
以Zn(NO3)·26H2O和AlCl3·6H2O为原料,借助CO(NH2)2的水解反应,采用化学均相共沉淀方法和热处理工艺,在自制CaSiO3∶Pb,Mn红色荧光粉表面包覆ZnO∶Al,形成透明导电层。
2.
In order to overcome these drawbacks, two methods are mainly employed: substitution and surface modification.
为了克服这方面的缺点，目前主要有两种改进手段：体相掺杂和表面包覆。
6) coated
[英]['kəutid] [美]['kotɪd]
表面包覆
1.
The influence of surfactant and coated Al(OH) 3 on dispersion behavior of graphite in aqueous slurries was investigated by Zeta potential, contact angle, sedimentation and rheological measurement.
利用ζ电位、润湿性、沉降性、流变学测试研究了表面活性剂、表面包覆Al(OH) 3对天然鳞片石墨在水中分散性的影响。
2.
In this paper, heterocoagulation is applied in coating aluminum hydroxide on natual flaky graphite and coated graphite is produced.
探讨了影响石墨表面包覆效果的关键因素 ,结果表明 ,pH值、处理温度和涂层物质前驱体的加入量是影响包覆效果的关键因素。
3.
The MgO-coated LiCoO 2 was analyzed by SEM and photoelectron spectrum.
通过湿化学方法首先制得锂离子电池正极材料LiCoO2 ,以MgSO4 和氨水为原料对LiCoO2 进行表面包覆得到MgO包覆LiCoO2 样品。
补充资料：有机覆层:有机覆层
在基体材料表面覆以有机材料的材料保护层。在机械製造中﹐有机覆层的绝大部分是涂装层﹐或称油漆层。此外﹐也有用橡胶或塑料作为覆层的。需要抗酸﹑硷和抗腐蚀性气体和液体的钢铁件﹐常用厚约 3毫米的橡胶(如氯丁橡胶)或塑料(如氯化亚乙烯共聚物)黏在表面﹐可长期保护基体不受腐蚀。这种覆层主要用在大型抗蚀容器或排气系统中。埋在土壤中的金属构件﹐常以聚乙烯带包裹保护。在喷鉬或喷不锈钢的表面上涂覆聚四氟乙烯﹐在150℃温度下摩擦係数很低﹐磨损轻微﹐适於製造低载荷和要求高度清洁的滑动轴承﹐或用在食品﹑精细包装和纺织机械上。各国的Du﹑Dx轴承都是以塑料与金属复合製成的。通过静电喷涂将环氧树脂﹑氯化聚醚﹑聚四氟乙烯以及聚氯乙烯等塑料粉末涂覆在金属表面﹐可获多种抗化学腐蚀性极好的覆层﹐可用於输水﹑污水处理和海洋平台的设备上。有机覆层在辉光放电情况下﹐有机单体可以聚合成无针孔的有机膜﹐用作电容器的介质层。