1) surface ball milling coating method
球磨表面包覆
2) coating
[英]['kəʊtɪŋ] [美]['kotɪŋ]
表面包覆
1.
Through the thermodynamic anal ysis of coating process,it was proved that Al(OH)3 nucleus coating Ti(OH)4 c ompetes with Al(OH)3 film coating Ti(OH)4.
热力学分析表明,在纳米Ti(OH)4表面包覆Al(OH)3的过程中,存在核包覆和膜包覆的竞争;而在其它条件不变的情况下,包覆物的过饱和度对包覆形态起到了决定性的影响。
2.
Through the thermodynamic analysis of coating process, it was proved that Al_2O_3 nucleus coating TiO_2 competes with Al_2O_3 film coating TiO_2.
热力学分析表明,用化学液相沉积法在纳米TiO2表面包覆氧化铝的过程中,存在核包覆和膜包覆的竞争;而在其它条件不变的情况下,包覆物的过饱和度对包覆形态起到了决定性的影响。
3.
Studies were focused on the effects of different amounts of cobalt coating on structure and electrochemical characteristics of Ni(OH)_2.
通过“管道式合成”工艺制备了球形氢氧化镍,然后以化学沉积法在氢氧化镍表面包覆氢氧化钴,制备了表面覆钴含量不同(0。
3) surface coating
表面包覆
1.
Research on surface coating of nanoscale titania;
纳米二氧化钛表面包覆的研究
2.
Effect of surface coating by ball milling on cycle stability of Mg-based hydrogen storage electrodes;
球磨表面包覆对镁基贮氢合金电化学性能的影响
4) Surface modification
表面包覆
1.
Surface modification of CaSiO3∶Pb, Mn phosphors was carried out by coating transparent conductive films of Al-doped zinc oxide which were formed by homogeneous phase co-precipitation and heat treatment process.
以Zn(NO3)·26H2O和AlCl3·6H2O为原料,借助CO(NH2)2的水解反应,采用化学均相共沉淀方法和热处理工艺,在自制CaSiO3∶Pb,Mn红色荧光粉表面包覆ZnO∶Al,形成透明导电层。
2.
In order to overcome these drawbacks, two methods are mainly employed: substitution and surface modification.
为了克服这方面的缺点，目前主要有两种改进手段：体相掺杂和表面包覆。
5) coated
[英]['kəutid] [美]['kotɪd]
表面包覆
1.
The influence of surfactant and coated Al(OH) 3 on dispersion behavior of graphite in aqueous slurries was investigated by Zeta potential, contact angle, sedimentation and rheological measurement.
利用ζ电位、润湿性、沉降性、流变学测试研究了表面活性剂、表面包覆Al(OH) 3对天然鳞片石墨在水中分散性的影响。
2.
In this paper, heterocoagulation is applied in coating aluminum hydroxide on natual flaky graphite and coated graphite is produced.
探讨了影响石墨表面包覆效果的关键因素 ,结果表明 ,pH值、处理温度和涂层物质前驱体的加入量是影响包覆效果的关键因素。
3.
The MgO-coated LiCoO 2 was analyzed by SEM and photoelectron spectrum.
通过湿化学方法首先制得锂离子电池正极材料LiCoO2 ,以MgSO4 和氨水为原料对LiCoO2 进行表面包覆得到MgO包覆LiCoO2 样品。
6) surface coating method
表面包覆法
1.
A series of γ Fe 2O 3 particles coated with different contents of barium ferrite have been prepared by the surface coating method.
采用表面包覆法合成了一系列不同包覆量的ＢａＦｅ１２Ｏ１９－γ－Ｆｅ２Ｏ３复合磁粉，采用Ｘ射线粉末衍射（ＸＲＤ）对样品进行物相分析，用振动样品磁强计（ＶＳＭ）测试样品磁性能，得到矫顽力和比饱和磁化强度随包覆量变化的关系曲线，由此讨论了过渡层的存在对样品磁性能的影响以及不同焙烧工艺条件下，样品磁性能的变化规律。
补充资料：赖氨酸面包
在谷物粮食的植物蛋白中，氨基酸组成不合理，一般普遍缺乏赖氨酸。为了弥补粮食蛋白的缺陷，增加食品营养，近年来出现了“特殊营养食品”——赖氨酸食品。
赖氨酸面包的生产方法采用二次发酵法较好，即在第二次和面时加入强化剂赖氨酸。现出售的赖氨酸主要是晶体状的白色颗粒，每公布价格30元左右，由于添加量较小，则每个100克面包成本大约提高2～3分钱。
工艺流程 酵母、糖、盐 剩余面粉、糖、盐及其它辅料
↓ ↓
面粉→第一次和面→第一次发酵→第二次和面→第二次发酵
↑ (28℃、3小时) ↑ (28℃、2小时)
水 赖氨酸 ↓
切块
↓
包装←冷却←烘烤←醒发←整形
(30～38℃、1小时)
在使用赖氨酸之前先检查其纯度，然后再算出加入0.4%的赖氨酸所需的赖氨酸实际量。使用时将其溶于30℃的温水后，即可使用。一般第二次和面加入0.4%的赖氨酸，就可使面包的营养价值提高一倍左右。
产品特点 制得的赖氨酸面包成品、色、味、香、形俱佳，是老弱病残、婴幼儿等人人皆宜的一种营养食品。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条