2) titanium-silica dioxide composite films
氧化钛-氧化硅复合薄膜
3) TiO_2/SiO_2 composite films
氧化钛/氧化硅复合薄膜
4) polysiloxane composite membrane
聚硅氧烷复合膜
1.
Two new polysiloxane composite membranes containing cyclic and acyclic polyamides modified pH glass electrode were prepared by sol-gel technology.
用溶胶 凝胶技术制备了两种新的含环状和非环状多酰胺的聚硅氧烷复合膜改性的 pH玻璃电极 。
5) composite oxide film
复合氧化膜
1.
In an electrolyte containing micro crystalline silicates,an inlay Si composite oxide film was formed by single electrolysis of aluminum matrix surface and a protective and colored film was made by electrolysis-coloring of this oxide film in another electrolyte containing metal salt/Si-complex.
在含有硅超微粒子的电解液中,采用电化学方法对铝或铝合金进行一次电解,在其表面获得掺硅复合氧化膜,并在含有混合金属盐和硅配合体系中进行二次电解着色,获得具有高防护性的彩色复合铝氧化膜。
2.
In this paper,the chemical fabricating methods,the growth mechanism of composite oxide films on aluminum,the focus of current research and prospective development about the technology of forming composite oxide films with high.
目前通过电化学方法增大铝阳极箔的有效表面积已越来越困难,铝电解电容器的阳极箔正面临一场新的技术革新:形成高介电常数的复合氧化膜来提高铝氧化膜的比容。
6) composite anodizing film
复合氧化膜
1.
The composite anodizing film of Al_2O_3-PTFE is prepared by high voltage anodization in mixed acid electrolyte containing polytetrafluoroethylene(PTFE) emulsion.
结果表明,复合氧化膜具有较好的耐蚀性能;扫描电镜(SEM)结果显示,氧化膜的孔径为250~300 nm,有利于电解液中超细粉体的填充;添加了PTFE乳液后,铝阳极氧化多孔膜能部分或全部被PTFE微粒所填充;膜的电子能谱分析结果也表明PTFE已结合进入多孔膜层,形成了Al2O3-PTFE复合氧化膜。
补充资料：氮化硅晶须补强碳化硅陶瓷复合材料
分子式：
CAS号：
性质：以碳化硅陶瓷为基体，以氮化硅晶须为增强体的复合材料。它既保留了碳化硅陶瓷优良的耐高温、抗蠕变、抗氧化、抗化学腐蚀、耐磨等性能，又具有比碳化硅陶瓷更高的强度和韧性，最高使用温度可达1400℃以上。由于氮化硅晶须与碳化硅陶瓷基体具有较好的物理相容性，化学性质相近，界面的结合力较强。该复合材料的烧结温度高，界面控制困难，成本高，主要用于航空、航天领域的高温部件。
CAS号：
性质：以碳化硅陶瓷为基体，以氮化硅晶须为增强体的复合材料。它既保留了碳化硅陶瓷优良的耐高温、抗蠕变、抗氧化、抗化学腐蚀、耐磨等性能，又具有比碳化硅陶瓷更高的强度和韧性，最高使用温度可达1400℃以上。由于氮化硅晶须与碳化硅陶瓷基体具有较好的物理相容性，化学性质相近，界面的结合力较强。该复合材料的烧结温度高，界面控制困难，成本高，主要用于航空、航天领域的高温部件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。