1) High temperature baking
高温烘烤
1.
Analysis of silver coating yellowing after high temperature baking;
镀银层高温烘烤发黄原因分析
2) baking temperature
烘烤温度
1.
The effect of baking temperature on the crystal structure and ferroelectric properties of Bi_ (3.25)La_( 0.75)Ti_3O_(12) thin films prepared by sol-gel processing;
烘烤温度对溶胶-凝胶法制备镧掺杂钛酸铋薄膜结构与铁电性质的影响
2.
LaNiO3(LNO) thin films were prepared on Si(100) substrates with various baking temperatures from 150 ℃ to 300 ℃ by sol-gel route.
利用X射线粉末衍射、原子力显微镜、扫描电子显微镜和四探针电阻测量法研究了不同烘烤温度对LaNiO3薄膜的晶体结构、表面形貌和导电性能的影响。
3.
The experimental results show that there are four kinds of microscopic process in baking process and the effect of baking temperature is determined by the integrated influence of these four microscopic processes.
采用正电子湮没技术研究了烘烤温度对 ELC—BH 钢板烘烤硬化性的影响,指出了烘烤期间钢板中可能存在四种不同的微观变化过程。
3) dielectric drying
高频烘烤
4) baking temperature and humidity
烘烤温湿度
1.
Effect of baking temperature and humidity change on leaf membrane lipid peroxidation to the different varieties of flue-cured tobacco
烘烤温湿度变化对不同烤烟品种烟叶膜脂过氧化作用的影响
6) baking temperature uniformity
烘烤温度均质性
补充资料：烘烤硬化性
烘烤硬化性
bake hardening ability
hongkao yinghuaxing烘烤硬化性(bake hardening ability)薄钢板经过冲压加工、涂漆和低温烤漆后屈服强度能有所提高的性能，又称烤漆硬化性，简称BH性。具有烘烤硬化性的薄钢板的原始屈服强度可以较低，以利于进行冲压加工，经冲压、涂漆和温度为17。~200℃，时间为20~3omin的低温烘烤后，屈服强度通常可提高40~80MPa。具有供烤硬化特性的钢主要有4类:氮化钥，含磷的铝镇静，双相钢和特生产的超低碳钢。 烘烤硬化主要是钢中残留的固溶碳和氮原子所引起的时效的结果。在钢板的铁原子点阵中有向隙固溶碳和氮原子。经过变形，固溶体点阵中产生了位错线。低温烘烤处理，促进了碳、氮原子间位错线的张力区扩散，形成气团，钉扎住位错，增加了进一步开动位错的应力，这在宏观上就表现为钢板强度的提高。生产上主要是通过控制钢的碳含量，控制冷轧后的退火温度、时间和冷却速度而调整碳原子在铁原子点阵中的固溶量，达到使钢无常温时效但有高温时效的效果，进而得到供烤硬化性。 烘烤硬化性能对现代汽车车身覆盖件的制造十分有利。应用具有烘烤硬化性的钢板冲制车身零件，可以降低冲压负荷，减薄车身钢板的厚度，而车身的强度和刚度并不下降，这对于车身上的一些浅冲压件的冲制更为重要。由于因加工硬化产生的强度增加十分有限。在这些浅冲压件的中心，塑性变形程度通常不到5%。供烤硬化恰好弥补了这一不足，使车身整体能够达到较高的强度水平。 (唐获)