1) Seawater corrosion fatigue
海水腐蚀疲劳
2) corrosion fatigue
腐蚀疲劳
1.
Mechanism of corrosion fatigue for as-extruded magnesium alloy AZ80;
变形镁合金AZ80的腐蚀疲劳机理
2.
A Study on Corrosion Fatigue Behavior in High Strength Aluminum Alloy LC4CS;
LC4CS高强铝合金腐蚀疲劳行为研究
3.
Study on the law of fatigue stiffness decay of reinforced concrete beams subjected to corrosion fatigue;
混凝土梁腐蚀疲劳刚度衰减规律
3) corrosion-fatigue
腐蚀疲劳
1.
The way was established to decompose DFR-corrosion-influence-factor into ground-corrosion-influence-factor and air-corrosion-fatigue-influence-factor.
为使腐蚀环境下民机结构疲劳分析的细节疲劳额定值(DFR)方法具有更广泛适用性,对DFR腐蚀影响系数与腐蚀环境的关系进行了研究,将DFR的腐蚀影响系数分解为地面停放腐蚀影响系数和空中腐蚀疲劳影响系数,建立了地面停放腐蚀影响系数与地面停放腐蚀时间的关系,以及空中复杂综合环境腐蚀疲劳影响系数与单一介质环境腐蚀影响系数的关系。
2.
Analysis of the cracks on outside surface of 4340 steel super-high pressure thick-walled pipe bend after 17 years service showed that, these cracks are of corrosion-fatigue cracks in cooling water under the affect of residual tensile stress formed in cold bending.
对高压聚乙烯装置中的４３４０钢超高压厚壁管弯头外表面裂纹的分析表明，裂纹属于冷却水介质中的腐蚀疲劳开裂。
3.
The investigation of corrosion-fatigue life on aircraft structures mainly depends on the tests and analyses by substituting typical structural parts(fatigue + corrosion) for the full-scale structures.
飞机结构腐蚀疲劳寿命研究主要依靠典型结构件(疲劳+腐蚀)代替全尺寸机体结构进行试验和分析,因此,在机场总体环境谱基础上进一步分析飞机局部环境谱有着重要意义。
4) fatigue corrosion
腐蚀疲劳
1.
The fatigue corrosion behavour of 2024T3 aluminum alloy test pieces is studied in the acidic sodium chloride solution of 45℃ and pH=3.
通过实验研究了 2 0 2 4 -T3铝合金四种表面防护处理工艺的腐蚀疲劳性能 。
5) prior-corroded fatigue
预腐蚀疲劳
6) Fatigue failure of hot corrosion
热腐蚀疲劳
补充资料：海水腐蚀
分子式：
CAS号：
性质：金属在海水中所发生的腐蚀。海水是一种典型的电解质溶液，对金属的腐蚀具有电化学本质。由于海水中含有大量的氯离子，能破坏金属表面的钝化膜，故腐蚀的阳极过程阻滞很小，腐蚀速度相当大，而腐蚀的阴极过程是氧去极化作用。在静态或低流速下，铸铁和钢在海水中的腐蚀完全取决于阴极的阻滞，一般受氧扩散的控制。
CAS号：
性质：金属在海水中所发生的腐蚀。海水是一种典型的电解质溶液，对金属的腐蚀具有电化学本质。由于海水中含有大量的氯离子，能破坏金属表面的钝化膜，故腐蚀的阳极过程阻滞很小，腐蚀速度相当大，而腐蚀的阴极过程是氧去极化作用。在静态或低流速下，铸铁和钢在海水中的腐蚀完全取决于阴极的阻滞，一般受氧扩散的控制。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条