1) corrosion and heat fatigue
腐蚀热疲劳
1.
It was concluded that it was corrosion and heat fatigue that caused the bursting.
通过对某电厂水冷壁爆管试样的宏观形貌、化学成分、显微组织、断口形貌等的分析,得出其发生爆管的主要原因是外界热冲击导致的腐蚀热疲劳。
2) Fatigue failure of hot corrosion
热腐蚀疲劳
3) corrosion thermal fatigue
腐蚀性热疲劳
1.
2 boilers in Ningxia Dawukou Power Plant, points out that the failure of water-cooling wall tubes is due to the factors of vibration during the start and stop of the boiler and the high sulfur in coal etc, results in the corrosion thermal fatigue on flue gas side, puts forward relevant counter measures.
通过对国电宁夏大武口发电厂#1、#2炉水冷壁管存在的横向裂纹现象进行宏观检验、化学分析、力学性能、金相显微组织分析,指出水冷壁管横向裂纹的主要原因是由于运行过程中存在启停振动、燃煤含硫量偏高等因素,导致水冷壁管在运行过程中产生烟气侧腐蚀性热疲劳。
4) corrosion fatigue
腐蚀疲劳
1.
Mechanism of corrosion fatigue for as-extruded magnesium alloy AZ80;
变形镁合金AZ80的腐蚀疲劳机理
2.
A Study on Corrosion Fatigue Behavior in High Strength Aluminum Alloy LC4CS;
LC4CS高强铝合金腐蚀疲劳行为研究
3.
Study on the law of fatigue stiffness decay of reinforced concrete beams subjected to corrosion fatigue;
混凝土梁腐蚀疲劳刚度衰减规律
5) corrosion-fatigue
腐蚀疲劳
1.
The way was established to decompose DFR-corrosion-influence-factor into ground-corrosion-influence-factor and air-corrosion-fatigue-influence-factor.
为使腐蚀环境下民机结构疲劳分析的细节疲劳额定值(DFR)方法具有更广泛适用性,对DFR腐蚀影响系数与腐蚀环境的关系进行了研究,将DFR的腐蚀影响系数分解为地面停放腐蚀影响系数和空中腐蚀疲劳影响系数,建立了地面停放腐蚀影响系数与地面停放腐蚀时间的关系,以及空中复杂综合环境腐蚀疲劳影响系数与单一介质环境腐蚀影响系数的关系。
2.
Analysis of the cracks on outside surface of 4340 steel super-high pressure thick-walled pipe bend after 17 years service showed that, these cracks are of corrosion-fatigue cracks in cooling water under the affect of residual tensile stress formed in cold bending.
对高压聚乙烯装置中的４３４０钢超高压厚壁管弯头外表面裂纹的分析表明，裂纹属于冷却水介质中的腐蚀疲劳开裂。
3.
The investigation of corrosion-fatigue life on aircraft structures mainly depends on the tests and analyses by substituting typical structural parts(fatigue + corrosion) for the full-scale structures.
飞机结构腐蚀疲劳寿命研究主要依靠典型结构件(疲劳+腐蚀)代替全尺寸机体结构进行试验和分析,因此,在机场总体环境谱基础上进一步分析飞机局部环境谱有着重要意义。
6) fatigue corrosion
腐蚀疲劳
1.
The fatigue corrosion behavour of 2024T3 aluminum alloy test pieces is studied in the acidic sodium chloride solution of 45℃ and pH=3.
通过实验研究了 2 0 2 4 -T3铝合金四种表面防护处理工艺的腐蚀疲劳性能 。
补充资料：腐蚀
分子式：
CAS号：
性质： 材料与它所处的环境发生作用而产生的损坏。不仅金属材料会因腐蚀而损坏，而且非金属材料(如塑料、混凝土及木材等)也会因发生腐蚀而损坏。但在工业上，金属及其合金至今仍然是最主要的结构材料。金属因腐蚀造成的直接损失是巨大的，估计全世界每年约有相当于年产量10％的钢铁由于腐蚀而报废。腐蚀通常是指金属的损坏。
CAS号：
性质： 材料与它所处的环境发生作用而产生的损坏。不仅金属材料会因腐蚀而损坏，而且非金属材料(如塑料、混凝土及木材等)也会因发生腐蚀而损坏。但在工业上，金属及其合金至今仍然是最主要的结构材料。金属因腐蚀造成的直接损失是巨大的，估计全世界每年约有相当于年产量10％的钢铁由于腐蚀而报废。腐蚀通常是指金属的损坏。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条