1) high-temperature resistant property
高温抗裂性
2) hot tear resistance
抗高温撕裂性
3) High Temperature Resistance
抗高温性
4) low temperature crack resistance
低温抗裂性
1.
Compared with basal and modified asphalt mixture,the performances of high modulus asphalt mixture,including high temperature stability,low temperature crack resistance and dynamic modulus in different temperature and variable loading frequency,are analyzed by dint of experiment and study which considers the material ingredient and designing methods.
从高模量沥青混合料的材料组成及配合比设计出发,通过与基质沥青混合料和几种改性沥青混合料路用性能的对比,利用试验方法分析了高模量沥青混合料材料的高温稳定性、低温抗裂性以及不同温度和加载频率下的动态模量。
5) low temperature anti-cracking performance
低温抗裂性
1.
To ensure low temperature anti-cracking performance of asphalt treated base,the low temperature anti-cracking performance of three kinds of aggregate graduation ATB30 were comprehensively evaluated by freeze and thaw low temperature (-15 ℃、-5 ℃、5 ℃、15 ℃) split test and low temperature(-15 ℃、-10 ℃、-5 ℃、0 ℃、5 ℃、10 ℃、15 ℃) bend test.
为了确保沥青稳定碎石基层的低温抗裂性,对3种ATB30级配进行了冻融后低温(-15℃、-5℃、5℃、15℃)劈裂试验和低温(-15℃、-10℃、-5℃、0℃、5℃、10℃、15℃)弯曲试验,全面评价了ATB30的低温抗裂性。
2.
This paper carries out the bending beam and creep deformation tests under low temperature for the different aggregate grading materials in stress absorbing layers with inventive Sampave asphalt and the other two modified asphalts and then analyzes the influences of asphalt binder and aggregate grading on low temperature anti-cracking performances.
通过对自主研发的Sampave等3种改性沥青结合料和不同级配的应力吸收层沥青混合料进行低温弯曲和低温蠕变试验,分析沥青结合料和矿料级配对应力吸收层沥青混合料低温抗裂性能的影响。
补充资料：高温抗氧化涂层
分子式：
CAS号：
性质：高温下能阻止或减少氧化气氛对材料表面氧化的涂层总称。按其抗氧化作用的时效和被保护基体抗氧化的要求，分为暂时性抗氧化和长期抗氧化涂层两类。按其组成，有硅化物涂层、铝化物涂层、高温搪瓷涂层、高温烧结涂层等。涂层的保护作用是由于涂层是一个能阻止氧化气氛扩散的阻挡层。这类涂层可使工件能在原先不能工作的环境中使用，或可延长工件的使用寿命。
CAS号：
性质：高温下能阻止或减少氧化气氛对材料表面氧化的涂层总称。按其抗氧化作用的时效和被保护基体抗氧化的要求，分为暂时性抗氧化和长期抗氧化涂层两类。按其组成，有硅化物涂层、铝化物涂层、高温搪瓷涂层、高温烧结涂层等。涂层的保护作用是由于涂层是一个能阻止氧化气氛扩散的阻挡层。这类涂层可使工件能在原先不能工作的环境中使用，或可延长工件的使用寿命。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。