1) Si/SiO 2 multilayers
硅/二氧化硅多层膜
2) silica coating
二氧化硅膜层
3) silica membrane
二氧化硅膜
1.
Methyl-modified silica membranes were prepared by acid catalysed co-hydrolysis and condensation reaction of tetra-ethylortho-silicate(TEOS) and methyl-tri-ethoxy-silane(MTES) in ethanol and characterized by TGA,FTIR and gas permeation.
用甲基三乙氧基硅烷(MTES)代替部分正硅酸乙酯(TEOS)作为前驱物,通过共水解缩聚反应可制得甲基修饰的二氧化硅膜。
2.
Microporous silica membranes on Υ-Al2O3/α-Al2O3 porous supports were prepared by a sol-gel process, and characterized by IR, TG, FE-SEM,N2 adsorption as well as gas permeation.
利用溶胶-凝胶法在Υ-Al2O3/α-Al2O3多孔支撑体上合成了微孔二氧化硅膜,并用IR、TG、FESEM、N2吸附以及气体渗透等手段对二氧化硅膜进行了研究。
3.
The surface wettability,surface structure and water absorbed amount of the silica membranes were investigated.
以正硅酸乙酯(TEOS)、甲基三乙氧基硅烷(MTES)为硅源,硝酸为催化剂,制备了甲基修饰的二氧化硅膜,研究了MTES改性二氧化硅膜的表面润湿性与表面结构的关系以及MTES改性二氧化硅膜的吸水率。
4) silica film
二氧化硅膜
1.
Synthesis of silica film using tetraethylorthosilicate;
利用正硅酸乙酯制备二氧化硅膜
6) Ge/silicon oxide nanometer multilayer films
锗/氧化硅纳米多层膜
1.
Ge/silicon oxide nanometer multilayer films were deposited by the r.
用射频磁控溅射法制备了锗/氧化硅纳米多层膜,在室温下测量了Au/锗/氧化硅纳米多层膜/p-Si结构的电致发光。
2.
Ge/silicon oxide nanometer multilayer films are deposited by the r.
测量到了来自Au/锗/氧化硅纳米多层膜/p-Si结构的电致黄光发射,并发现该纳米结构具有整流特性。
补充资料：全氟羧酸-磺酸多层阳离子交换膜
分子式：
CAS号：
性质：又称全氟羧酸-磺酸多层阳离子交换膜，需在膜的一面形成一羧酸膜层。其制法是将全氟磺酸膜片与全氟羧酸膜片加热层压而成，或在全氟磺酸膜的一面经化学处理，使—SO3H转换成—COOH基。这种离子膜一面为—SO3H基，另一面为—COOH，用聚四氟乙烯织物增强，在氯化钠电解制碱中的电流效率为95%左右。
CAS号：
性质：又称全氟羧酸-磺酸多层阳离子交换膜，需在膜的一面形成一羧酸膜层。其制法是将全氟磺酸膜片与全氟羧酸膜片加热层压而成，或在全氟磺酸膜的一面经化学处理，使—SO3H转换成—COOH基。这种离子膜一面为—SO3H基，另一面为—COOH，用聚四氟乙烯织物增强，在氯化钠电解制碱中的电流效率为95%左右。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条