1) precipitation method of oxalate
草酸盐沉淀法
1.
Ultra fine LaPO_4∶Eu powder was prepared by precipitation method of oxalate.
采用草酸盐沉淀法制备超微发光粉体La-PO4∶Eu。
2) oxalate coprecipitation method
草酸盐共沉淀法
1.
BaTiO3 powder was synthesized by oxalate coprecipitation method,and through the experiment and characterizations of XRD,DTA-TG,IR,TEM the result indicated that the product BaTiO3 was cube,well-proportioned and the size was about 30nm and reunited less.
利用草酸盐共沉淀法合成BaTiO3纳米粉体,通过XRD分析、DTA-TG分析、IR分析及TEM形貌分析等分析手段,对制得的粉体进行了表征和测试,结果表明合成的BaTiO3粉体为单纯的立方相,粒径均匀,颗粒大小在30 nm左右,无严重的团聚现象。
2.
In order to develop more effective,nontoxic and environment-friendly inorganic luminescent nanomaterials for manifesting fingerprint,the Eu3 + doped LaPO4 nano-materials were synthesized by oxalate coprecipitation method.
为了研究新型高效的、对人体无毒、对环境无污染的显现指印的无机纳米荧光材料,采用草酸盐共沉淀法制备纳米发光材料LaPO4∶Eu3+,并利用PAMAM树形分子配置LaPO4∶Eu3+/PAM-AM G5。
3) oxalate precipitation
草酸盐沉淀
1.
The oxalate precipitated method can get oxalate precipitation by adding oxalic acid intodissolvable zirconic acid of a suitable amount or NH4OH into the solution of zirconium oxalate complex, andunder less than 400t,the ZrO2 powders can be given.
采用热质联用技术（ＴＧ—ＤＴＡ—ＭＳ）对草酸盐沉淀法和草酸盐络合物喷雾法两种制备超细ＺｒＯ２粉的热分解过程进行了研究实验得到了草酸锆沉淀产物和络合物喷雾干燥产物热分解过程中逸出的气体正离子质谱Ｏ＋，Ｈ２Ｏ＋，ＣＯ＋，随温度变化的话图以及相应的热重和差热曲线。
5) oxalate Co-precipitation
草酸盐共沉淀
1.
0 in starting materials,and the precursors were calcined at 700 ℃ for 4 h using temperature programming method through oxalate Co-precipitation route.
以Ti(OC4H9)4作钛源,Ba(Ac)2、BaCl2或Ba(NO3)2作钡源,采用草酸盐共沉淀法制备BaTiO3粉体。
6) oxalate gel coprecipitation
草酸胶态沉淀法
补充资料：铬盐沉淀-锌置换法提铊
铬盐沉淀-锌置换法提铊
extraction of thallium by chromate precipitation-zinc cementation
geyan Chendianxrnzhihuanfa tita铬盐沉淀一锌置换法提花(extraetion of thal-lium by ehromate PreeiPitation一zine eementa-tion)含花(I)硫酸盐溶液经铬盐沉淀、硫酸分解、锌粉置换产出金属铭的过程。如起始原料为铭烟尘时，一般先经碱熔炼、硫酸浸出获得含佗(I)硫酸盐溶液后再往下一步处理。 秘鲁中部矿业公司(Centromin Peru SA)采用这种方法从含佗的炼铅鼓风炉烟尘中回收佗，其工艺流程如图。 在火法炼铅过程中收得的含蛇烟尘，配加苏打、碳及铜屑，放在反射炉中进行碱熔炼，料中的锭再次挥发进入烟气得到进一步富集。从烟气收得的烟尘用硫酸浸出，得到含铂达159/L的T12SO;浸出液。向T12SO。浸出液加入铬盐NaZCrO;或K:CrO‘沉淀剂，在调节浸出液酸度至含游离硫酸3~49/L时，便发生铬酸佗的沉淀: T12SO;+NaZCrO4— T12CrO;今+NaZSO4过滤所得的铬酸蛇沉淀物须经两次硫酸分解与锌粉置换。第一次于363K温度下用20%浓度的硫酸分解T12Cro、沉淀物及返回的第一次锌粉置换所得的不纯海绵蛇。第二次用50%浓度的硫酸再分解1~2h。过滤所得的滤液先加NaZS净化除去重金属杂质，再进行罕瓜刀沉淀物 1 11述四，佩珊尸卜，Na0H Na，CrO，~州钻盐沉花11占 L-eeee.习卯.99%佗 铬盐沉淀一锌置换法提佗流程二次锌粉置换。置换所得海绵佗，加NaOH在593K温度下熔炼，即可获得纯度为”.99%的金属佗。 如硫酸浸出液含铁和砷过多，可用过量高锰酸钾将液中佗(I)氧化到佗(l)而获得Tl(OH):沉淀物。铁留在溶液中与蛇分离。所得沉淀物中会含有Mn02、砷、锑、锡及锌等杂质，须用硫酸加以分解，使Tl(OH)3转变成T12sO4进入分解液与这些杂质分离。当蛇全部转入分解液后，再添加铁屑将花(里)还原为铭〔I)，然后再加铬盐沉淀剂，使蛇生成T12CrO‘沉淀析出，与留在分解液中的杂质进一步分离而再次得到富集。 铬盐沉淀置换法富集蛇的效果好，工艺简单，但仅适用于处理含佗较高的料液。如用于从含佗稀的溶液中沉淀富集铭时，虽能富集但效果不好。