1) oxalate coprecipitation
草酸共沉淀法
1.
The giant dielectric constant material CaCu3Ti4O12(CCTO) powder has been fabricated successfully by an oxalate coprecipitation method.
用草酸共沉淀法在700℃保温1 h制备出了单相CaCu3Ti4O12粉体。
2) oxalate coprecipitation method
草酸盐共沉淀法
1.
BaTiO3 powder was synthesized by oxalate coprecipitation method,and through the experiment and characterizations of XRD,DTA-TG,IR,TEM the result indicated that the product BaTiO3 was cube,well-proportioned and the size was about 30nm and reunited less.
利用草酸盐共沉淀法合成BaTiO3纳米粉体,通过XRD分析、DTA-TG分析、IR分析及TEM形貌分析等分析手段,对制得的粉体进行了表征和测试,结果表明合成的BaTiO3粉体为单纯的立方相,粒径均匀,颗粒大小在30 nm左右,无严重的团聚现象。
2.
In order to develop more effective,nontoxic and environment-friendly inorganic luminescent nanomaterials for manifesting fingerprint,the Eu3 + doped LaPO4 nano-materials were synthesized by oxalate coprecipitation method.
为了研究新型高效的、对人体无毒、对环境无污染的显现指印的无机纳米荧光材料,采用草酸盐共沉淀法制备纳米发光材料LaPO4∶Eu3+,并利用PAMAM树形分子配置LaPO4∶Eu3+/PAM-AM G5。
4) oxalate Co-precipitation
草酸盐共沉淀
1.
0 in starting materials,and the precursors were calcined at 700 ℃ for 4 h using temperature programming method through oxalate Co-precipitation route.
以Ti(OC4H9)4作钛源,Ba(Ac)2、BaCl2或Ba(NO3)2作钡源,采用草酸盐共沉淀法制备BaTiO3粉体。
5) oxalate gel coprecipitation
草酸胶态沉淀法
6) precipitation method of oxalate
草酸盐沉淀法
1.
Ultra fine LaPO_4∶Eu powder was prepared by precipitation method of oxalate.
采用草酸盐沉淀法制备超微发光粉体La-PO4∶Eu。
补充资料：草酸
| 草酸 oxalic acid 最简单的二元酸。分子式HOOCCOOH。广泛存在于自然界中，特别是植物中，例如草本植物、大黄属植物、酢浆草、菠菜等，并常以钾盐的形式存在。在人或肉食动物的尿中，草酸以钙盐或草尿酸的形式存在。此外，肾和膀胱结石中也含有草酸钙。无水草酸为无色晶体，有吸湿性；熔点189.5℃；在约157℃时升华；易溶于水，能溶于乙醚。商品草酸含两分子结晶水；无色晶体；熔点101.5℃，加热至100℃可失去结晶水；微溶于乙醚。草酸分子中两个羧基直接相连，具有一些特殊性质，例如，草酸具有还原性，可使高锰酸钾还原成二价锰，这一反应在定量分析中被用作测定高锰酸钾浓度的方法；草酸还可用作纤维、油脂和制革工业的漂白剂，也是利用它的还原性。草酸受热发生脱羧脱水，生成二氧化碳、一氧化碳和水。草酸能与许多金属形成溶于水的络合物。 工业上是由一氧化碳与氢氧化钠作用，先生成甲酸钠，再经迅速加热至300℃，即转变成草酸。将木屑等碳水化合物与浓氢氧化钠水溶液于240～285℃共热，也可生成草酸钠。在钒催化下碳水化合物经浓硝酸氧化，最终产物也是草酸。草酸可作铁锈、墨水迹的清洗剂和金属抛光剂。草酸锑可作媒染剂，草酸铁铵是印制蓝图的药剂。 |