2) in situ TiC
原位生TiC
3) in-situ TiC particles
原位TiC颗粒
1.
Refinement mechanism of in-situ TiC particles on the microstructure of spray formed 7075 Al alloys;
原位TiC颗粒细化喷射沉积7075铝合金组织的机理
2.
The effects of in-situ TiC particles on microstmcture and solution temperature of spray formed 7093 Al alloy were investigated.
采用喷射沉积方法制备含有3%(体积分数)原位TiC颗粒的TiC_p/7093铝基复合材料,经过热挤压变形后进行固溶处理。
3.
The grain sizes were measured using a mean linear intercept method and the effect of in-situ TiC particles on semi-solid microstructure of spray formed 7075 alloy was analyzed.
制备具有不同原位TiC颗粒含量的喷射成形7075铝合金,在610℃和620℃二次加热并保温30min,淬火固定其半固态组织后采用扫描电镜进行观察,利用平均截线法统计其平均晶粒尺寸,分析不同颗粒含量对喷射成形7075铝合金半固态组织的影响规律。
4) in-situ TiC particle
原位TiC颗粒
1.
91%, volumic fraction) alloy were studied, and the effect of in-situ TiC particles on the microstructure of spray-formed 7075 alloy was investigated.
研究表明,原位TiC颗粒不仅细化喷射成形组织,而且在二次加热保温过程中有效地阻碍晶界的移动,抑制了显微组织的粗化过程,在600℃保温60min后合金平均晶粒尺寸仍小于30μm,表现出良好的钉扎效应。
2.
the distribution and morphology of in-situ TiC particles in matrix of 7075 Al alloys were observed by TEM and the average grain sizes were measured using a mean linear intercept method.
采用原位反应近液相线铸造方法制备含有少量原位TiC颗粒的7075铝基复合材料,通过透射电镜观察合金中的原位TiC颗粒的分布与形貌,并利用平均截线法测量晶粒尺寸,研究原位颗粒对近液相线铸造7075铝合金铸态组织形成机制的影响。
6) in situ formation of TiC
原位形成TiC
补充资料：tic corrugated pipe
分子式：
CAS号：
性质：具有环形槽结构，断面呈波纹状的塑料管。按壁结构不同分双壁波纹管与单壁波纹管，无孔波纹管与有孔波纹管。有孔波纹管用作农田的暗沟排水管，无孔波纹管用作户外电线保护套管、配线槽以及输送某些液体和气体等，由于其壁薄可节约原材料并且强度较高。
CAS号：
性质：具有环形槽结构，断面呈波纹状的塑料管。按壁结构不同分双壁波纹管与单壁波纹管，无孔波纹管与有孔波纹管。有孔波纹管用作农田的暗沟排水管，无孔波纹管用作户外电线保护套管、配线槽以及输送某些液体和气体等，由于其壁薄可节约原材料并且强度较高。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条