1) dipping-hydrolysis method
提拉水解法
1.
Adoption of Ti(OC 2H 5) 4 precursors through the sol-gel process based on hydrolysis reactions of metal alkoxides, by the dipping-hydrolysis method, quite-evenly optical film can be coated on glass substrates.
将正钛酸乙酯 (Ti(OC2 H5) 4)基体 ,用提拉水解法在玻璃基底上镀制成均匀性好且具有较高折射率的光学膜。
2) Czochralski method
提拉法
1.
Growth of large Ti~(3+):BeAl_2O_4 laser crystals by Czochralski method
大尺寸掺钛铝酸铍(Ti~(3+):BeAl_2O_4)激光晶体的提拉法生长
2.
Tetragonal scheelite-type cadmium gadolinium tungstate CdGd2(WO4)4, CGW single crystal was grown by the Czochralski method.
用提拉法生长了四方晶系白钨矿结构的钨酸钆镉[CdGd2(WO4)4,CGW]晶体。
3.
GdVO4 single crystals weighted more than 50g along a-axis and c-axis were grown by Czochralski method.
采用提拉法沿a轴和c轴生长出无色透明的GdVO4单晶,质量均超过50g。
3) Czochralski
提拉法
1.
Modeling of Czochralski Single Crystal Growth Process Using Neural Network;
基于神经网络的提拉法钛单晶生长过程建模
2.
Single Crystal Growth of LiGaO_2 by Czochralski Method and Defects Characterization;
提拉法生长镓酸锂晶体及缺陷研究
3.
Nd:YAP and Tm:YAP crystal of b axis were grown by the Czochralski method,and the problem of crack was resolved by the optimum of thermal field,technical parameters of growth and cutting process.
采用提拉法生长了b轴方向的掺钕和掺铥铝酸钇(Nd:YAP和Tm:YAP)晶体,通过温场系统、生长工艺参数和切割工艺的优化,克服了晶体开裂的问题,晶体直径达到46mm;通过真空退火工艺,既显著减轻了紫外和可见区的色心吸收,又减小了晶体的应力,有助于克服晶体在加工过程中的开裂问题。
4) CZ method
提拉法
1.
A high quality sapphire with directions of[a-axis] and [0001][c-axis] was grown by CZ method.
本实验采用提拉法,在中频感应加热单晶炉内,进行了不同生长方向蓝宝石晶体的生长工作,分别取[11-20]和[0001]生长的晶体c面(0001)的晶片。
2.
A Nd: GGG crystal was grown by CZ method.
本文采用提拉法(CZ)生长了Nd:GGG晶体,并从理论上讨论了包裹物、提拉速度、晶体转速和降温速率等因素对晶体开裂的影响,最后给出了生长无开裂Nd:GGG晶体的最佳工艺参数:径向温度梯度越小越好,纵向温度梯度在0。
3.
Large size PbWO4 crystal ingots 35 mm×250 mm with no macro-defects by CZ method with RF h eating had been produced,and these ingots' impurity,defects and lengthways tra nsparency could be avoided.
用中频感应加热提拉法成功地生长了无宏观缺陷的大尺寸钨酸铅晶体(PWO),其晶体尺寸为35mm×250mm;确定了晶体生长工艺,其参数为籽晶取向犤001犦、提拉速度1。
5) Czochralski technique
提拉法
1.
In the present work, large-size γ-LiAlO_2 single crystal with dimension of 45×50mm~3 has been grown by Czochralski technique.
本文使用提拉法生长出了尺寸达45×50mm3 的γLiAlO2 单晶。
2.
Firstly, large-size γ-LiAlO_2 single crystal with dimension of 45×50mm~3 has been grown by Czochralski technique.
本文首先使用提拉法生长出了尺寸达45×50mm3的γLiAlO2单晶,然后采用Ga2O3作为掺杂剂,仍用提拉法生长出了三种不同掺镓浓度的LiAl1 xGaxO2(x=0。
3.
Yb∶YAG laser crystals are grown by the Czochralski technique.
对中频感应提拉法生长的不同掺杂浓度的Yb∶YAG晶体的比热和导热性能进行了测试。
6) Czochralski(CZ) method
提拉(CZ)法
补充资料：低压压热釜油脂水解法
分子式：
CAS号：
性质：早期常用的油脂水解工艺方法。油脂和水在压热釜中通入压力为1MPa的饱和蒸汽。温度达到该压力下的饱和温度(约180℃)。由于在此温度下水在油脂中的溶解度不够，要加入碱性催化剂，一般用钙、镁或锌的氧化物，以氧化锌较普遍。其实质是第一步生成上述碱土金属的皂，金属皂使油脂与水形成油包水型乳液。在上述条件下反应时间为10h左右，分批进行，分解率可达95％。当原料质量好时，所得的脂肪酸色泽浅，不经蒸馏即可直接用于制皂或其他产品。
CAS号：
性质：早期常用的油脂水解工艺方法。油脂和水在压热釜中通入压力为1MPa的饱和蒸汽。温度达到该压力下的饱和温度(约180℃)。由于在此温度下水在油脂中的溶解度不够，要加入碱性催化剂，一般用钙、镁或锌的氧化物，以氧化锌较普遍。其实质是第一步生成上述碱土金属的皂，金属皂使油脂与水形成油包水型乳液。在上述条件下反应时间为10h左右，分批进行，分解率可达95％。当原料质量好时，所得的脂肪酸色泽浅，不经蒸馏即可直接用于制皂或其他产品。