2) YBCO HTS films
YBCO高温超导薄膜
3) YBCO superconducting thick film
YBCO超导厚膜
4) YBCO semiconductor membrane
YBCO半导体薄膜
5) YBCO film
YBCO薄膜
1.
YBCO films have good performances in microelectronic devices etc.
YBCO薄膜应用于超导电子器件中表现出优良的性能,如超导量子干涉仪(SQUID)等。
2.
The YBCO films were directly deposited on the {110} < 011 > textured Ag substrates by an ultrasonic spray pyrolysis method using the modified device.
用自行研制的超声雾化装置在{110}<011>织构的Ag基带上直接沉积了YBCO涂层超导薄膜,结果发现一步沉积所得YBCO薄膜的表面有许多白色小颗粒,而且薄膜的织构和临界电流密度都较低,这是在900℃高温沉积过程中大量的Ag蒸发和扩散到YBCO膜层中所致。
3.
The critical current density of YBCO film is 7.
YSZ和YBCO薄膜都为C 轴取向和平面织构的 ,YSZ( 2 0 2 )和YBCO( 1 0 3 )的X射线 (扫描衍射峰的全宽半峰值分别为 2 0°和 1 2°。
6) YBCO thin film
YBCO薄膜
1.
Study on the superheating phenomenon of YBCO thin film;
关于YBCO薄膜过热现象的研究
2.
YBCO thin film has the advantages of high voltage drop tolerance per unit length and being hard to be destroyed after the complete quench as a current limitation element of a resistive type SFCL.
YBCO薄膜材料作为电阻型高温超导限流器的限流元件具有单位通流长度耐压高,失超后不易损毁等优点。
3.
In this work, YBCO thin films were deposited on LaAlO_3 (LAO) underlayers by PLD and Pt was sputtered as electrodes by rf-sputtering method.
本文利用脉冲准分子激光在LaAlO3单晶基片上淀积了YBCO和Zr/Ti为94/6的PZT铁电薄膜,并通过高频溅射将Pt蒸镀在PZT薄膜上作为上电极;用X射线衍射表征了该多层膜的晶相结构,测量了PZT的铁电性能和介电特性,讨论了PZT/YBCO薄膜的制备工艺,以及工艺条件对晶相结构和薄膜性能的影响。
补充资料：超导薄膜
| 超导薄膜 superconducting thin film 利用蒸发、喷涂等方法淀积的厚度小于1微米的超导材料。超导薄膜除几何尺寸与块状超导体不同外，其结构和超导性质也有较大差别。对于块状超导体，磁场穿透层很薄，可以忽略不计，具有完全的抗磁性。但是超导薄膜的磁场穿透层与薄膜相比，就不能忽略不计。此外，当超导薄膜厚度很小时（小于10纳米），它的超导临界转变温度将下降。 已实用的超导薄膜分为低温和高温两类。低温超导薄膜是制造电子器件的主要薄膜材料。与高温超导薄膜相比，其均匀性、一致性以及隧道结制备和集成电路工艺方面具有优势；在液氦温区由于热噪声低，故低温超导薄膜制成的电子器件灵敏度高，是高温超导薄膜器件所不及。低温超导薄膜又分为低熔点超导薄膜，如Pb、In、Sn、Al等低熔点金属及其合金薄膜；高熔点超导薄膜，主要是难熔金属及其合金薄膜，已应用的是Nb超导薄膜；化合物超导薄膜，具有实用价植的是NbN和Nb3Sn、Nb3Ge薄膜。高温超导薄膜在液氮温度下工作，已研究并有实用价值的有钇系薄膜、铋系薄膜和铊系薄膜。铊系氧化物是超导临界温度最高的超导体，达125K。高温超导薄膜的质量和性能均已达到相当高的水准，利用高温超导薄膜制成的超导量子干涉器和微波器件等，其性能均达到实用要求。 |