1) carbon contained pellets
含碳团矿
1.
Experimental studies on direct reduction of carbon contained pellets were performed under the carbon covered protective condition and open fired atmosphere.
在盖碳保护敞焰加热条件下，对含碳团矿进行试验研究，得到金属化率与加热时间、加热温度、料层厚度等参数间的定量关系，从而确定了球团还原时获得高金属化率的条件。
2) carbon-bearing pellet
含碳球团矿
3) carbon-containing chromite pellet
含碳铬矿球团
1.
Aimed at production of hot metal containing Cr from 20% to 40%, the carbon-containing chromite pellets made from three kinds of typical chromite were reduced at 1300 ℃ for 30 minutes and then melted at 1550~1600 ℃ for 10 minutes and the slag was separated.
以3种典型的铬矿为原料,生产铬的质量分数为20%～40%的铁水为目标,对含碳铬矿球团在1300℃温度下还原30min,然后在1550～1600℃温度下恒温10min,进行渣金分离。
4) synthetic chromite by carbon
含碳铬矿团块
1.
The effects of C/O mole ratio and basicity of slagmaking components of synthetic chromite by carbon on reductivity of Cr_(2)O_(3) and total reductivity at the temperature range from 1 250℃ to 1 450℃ are researched and so is the separating behavior of metal phase from slag phase after reduction.
在1250～1450℃高温范围内研究内配碳铬矿团块中Cr2O3还原率和总还原率与内配碳比和渣相碱度的关系,并分析了含碳铬矿团块还原过程中金属相和渣相聚集和分离状态的变化。
5) Carbon-bearing Iron Ore Pellets
含碳铁矿球团
6) Carbon-Bearing Briquette
含碳锰矿团块
补充资料：含不饱和碳碳键聚合物
分子式：
CAS号：
性质：含不饱和碳碳键的功能聚合物主要有三种类型，第一种为聚合物中不饱和键相互共轭，构成线性共轭聚合物，包括聚乙炔型、聚芳杂环和聚苯衍生物。这类聚合物多具有电子导电和光导电特性，经掺杂处理后导电率可以达到半导体，甚至金属导体范围。是重要的导电聚合物。第二种为不饱和键表现为多核芳香烃，或者多核杂环等共轭结构，而各共轭结构相互之间相对独立，处在饱和聚合物的侧链上。这种聚合物多表现出一定光导特性，如聚乙烯基咔唑，是重要的高分子光导材料。第三种为不饱和键在聚合物中孤立存在，如含有肉桂酸酯的聚合物，这种聚合物在紫外光照射下能够发生交联反应，是潜在的负性光刻胶，可以用于印刷制版和集成电路生产。碳碳双键中的π电子还具有配位能力，与过渡金属离子构成类似二茂铁型络合物。
CAS号：
性质：含不饱和碳碳键的功能聚合物主要有三种类型，第一种为聚合物中不饱和键相互共轭，构成线性共轭聚合物，包括聚乙炔型、聚芳杂环和聚苯衍生物。这类聚合物多具有电子导电和光导电特性，经掺杂处理后导电率可以达到半导体，甚至金属导体范围。是重要的导电聚合物。第二种为不饱和键表现为多核芳香烃，或者多核杂环等共轭结构，而各共轭结构相互之间相对独立，处在饱和聚合物的侧链上。这种聚合物多表现出一定光导特性，如聚乙烯基咔唑，是重要的高分子光导材料。第三种为不饱和键在聚合物中孤立存在，如含有肉桂酸酯的聚合物，这种聚合物在紫外光照射下能够发生交联反应，是潜在的负性光刻胶，可以用于印刷制版和集成电路生产。碳碳双键中的π电子还具有配位能力，与过渡金属离子构成类似二茂铁型络合物。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条