1) overall crack probability
体积开裂概率
1.
The paper analyses the anti cracking reliability in massive concrete structure with the concept of overall crack probability, presenting the cracking control design and construction combined with FEM.
运用体积开裂概率分析了大体积混凝土结构的抗裂可靠性，并结合有限元法对控制裂缝设计与施工进行了研究。
2) crack probability
开裂概率
1.
A concept of dry shrinkage crack probability (C) has been put forward by which the concrete dry shrinkage crack probability could be devided into three levels named as: C≥60%(high risk),40%≤C<60%(medium risk)and C<40%(low risk).
介绍了一种评价混凝土收缩开裂的试验和评价方法,该法能够准确测量约束状态下混凝土干燥收缩时其内部产生的拉应力,特别是能够客观评价补偿收缩混凝土在弹性限制条件下抵御收缩应力的能力;提出了干燥收缩开裂概率C的概念,并将混凝土发生干燥收缩开裂的概率划分为C≥60%(高开裂风险),40%≤C<60%(中等风险)和C<40%(低风险)三种状态;试验表明,补偿收缩混凝土能够在混凝土中建立一定的自应力,可以有效降低混凝土的干燥收缩开裂概率。
3) probability of shrinkage and crack
收缩开裂概率
4) crack opening volume (COV)
裂缝张开体积
5) probability of cracks
裂缝概率
6) fracture probability
断裂概率
1.
Aim To deduce the approximate functions of fatigue fracture probability, reliability and fatigue lifetime, and make nonequibrium statistical theory of fatigue fracture applicable to real metals.
目的推导出疲劳断裂概率、可靠性及疲劳寿命的近似解析表达式，使疲劳断裂的非平衡统计理论具有实际应用价值。
2.
According to the effection of hydrogen to the crackle s forming in metals,some important functions of fracture strain--fracture probability,reliability,and lifetime are discussed.
根据氢对金属中裂纹形核的影响 ,讨论了疲劳断裂的几个重要函数——疲劳断裂几率、可靠性及寿命 ,重点根据位错的堆积模型和详细的数学推导研究了氢致开裂纹的分布函数 ,导出了氢致裂纹的断裂概
补充资料：穿晶开裂
分子式：
CAS号：
性质：金属材料开裂的金属学特征之一。裂纹由晶粒内部穿过。延性断裂的断口微观特征一般为韧窝状，脆性断裂的特征为解理或准解理花样。
CAS号：
性质：金属材料开裂的金属学特征之一。裂纹由晶粒内部穿过。延性断裂的断口微观特征一般为韧窝状，脆性断裂的特征为解理或准解理花样。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条