1) arc ablate rate
电弧烧蚀速率
2) arc erosion rate
电弧腐蚀速率
1.
A new method was designed for the measurement of arc erosion rates of contact materials in this paper.
自行设计了电弧腐蚀速率的测量方法,避免了一般电弧腐蚀速率测量中存在的不足,并对真空断路器中常用的 CuCr25,CuCr50 触头材料以及纯 Cu 和纯 Cr 的电弧腐蚀速率进行了测量。
3) arc ablation
电弧烧蚀
1.
For improving the arc ablation resistance of nozzle materials of high-voltage circuit breaker,it is needed to fill Al 2 O 3 and TiO 2 in PTFE to reduce the ablation of arc energy and improve the arc ablation resistance of nozzle.
为了提高高压断路器喷口材料的耐电弧烧蚀性能,采用在聚四氟乙烯(PTFE)中添加三氧化二铝或二氧化钛,降低电弧能量对PTFE的烧蚀,同时试验研究复合聚四氟乙烯介电性能的变化规律。
4) arc erosion
电弧烧蚀
1.
It is found by XRD that the phase structure of La2NiO4 ceramics did not change after arc erosion and exhibited a high chemical stability.
X射线衍射分析发现La2NiO4陶瓷在电弧烧蚀作用下相结构不发生变化,具有高的化学稳定性。
2.
After cryogenic treatment,the resistance property of arc erosion of CuCr50 vacuum contact material change dramatically.
CuCr50真空触头材料经深冷处理后 ,抗电弧烧蚀性能明显提高。
3.
The samples of carbon sliding panel infiltrated with copper were prepared,and the friction test and arc erosion test were carried out.
制备了浸铜碳滑板试样,并通过试验研究了浸金属碳滑板和纯碳滑板的机械摩擦性能与电弧烧蚀性能。
5) ablation rate
烧蚀速率
1.
Some calculations and analysis for three examples under different ablation rates were demonstrated.
针对金属表面的烧蚀过程,采用一维传热模型,将物体内的传热、温度变化分为2个阶段,即物体被加热到熔点温度的阶段及物体开始烧蚀阶段,使用积分近似的分析方法,完整地建立了表面烧蚀速率与表面加热功率之间的近似计算关系式。
2.
The effects of the respective content of silica aerogel and boron-phenolic resin on the properties of EPDM/NBR flexible insulation material,such as tensile strength,elongation-to-break,mass ablation rate,linear ablation rate and relative density were analyzed and compared.
通过比较分析白炭黑与硼酚醛树脂用量对EPDM/NBR柔性绝热层材料拉伸强度、断裂伸长率、质量烧蚀速率和线烧蚀速率以及相对密度的影响,得出随着白炭黑或硼酚醛树脂用量的增加,柔性绝热层材料的拉伸强度和相对密度呈递增趋势,烧蚀速率呈递减趋势,断裂伸长率在白炭黑和FB用量各自为20份时有极大值。
6) micro-arc ablation
微电弧烧蚀
补充资料：弹头烧蚀(见弹头防热)
弹头烧蚀(见弹头防热)
warhead ablation
dantou shaoshi弹头烧蚀(warhead的lation)见弹头防热。